Microstructural evolution in nickel alloy C-276 after Ar-ion irradiation at elevated temperature | |
Jin, Shuoxue; He, Xinfu; Li, Tiecheng; Ma, Shuli; Tang, Rui; Guo, Liping | |
刊名 | MATERIALS CHARACTERIZATION |
2012 | |
卷号 | 72 |
关键词 | Irradiation damage Nickel-base alloy C-276 Multi-scale modeling Microstructure Super-critical water reactors |
ISSN号 | 1044-5803 |
DOI | 10.1016/j.matchar.2012.06.010 |
URL标识 | 查看原文 |
收录类别 | SCIE ; EI |
语种 | 英语 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/4098005 |
专题 | 武汉大学 |
推荐引用方式 GB/T 7714 | Jin, Shuoxue,He, Xinfu,Li, Tiecheng,et al. Microstructural evolution in nickel alloy C-276 after Ar-ion irradiation at elevated temperature[J]. MATERIALS CHARACTERIZATION,2012,72. |
APA | Jin, Shuoxue,He, Xinfu,Li, Tiecheng,Ma, Shuli,Tang, Rui,&Guo, Liping.(2012).Microstructural evolution in nickel alloy C-276 after Ar-ion irradiation at elevated temperature.MATERIALS CHARACTERIZATION,72. |
MLA | Jin, Shuoxue,et al."Microstructural evolution in nickel alloy C-276 after Ar-ion irradiation at elevated temperature".MATERIALS CHARACTERIZATION 72(2012). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论