Microstructure and microhardness evolution of a Mg(83)Ni(6)Zn(5)Y(6) alloy upon annealing

CORC > 金属研究所 > 中国科学院金属研究所

	Microstructure and microhardness evolution of a Mg(83)Ni(6)Zn(5)Y(6) alloy upon annealing
	X. H. Shao ; Z. Q. Yang ; J. H. You ; K. Q. Qiu ; X. L. Ma
刊名	Journal of Alloys and Compounds
	2011
卷号	509 期号:26 页码:7221-7228
关键词	Mg alloy Microstructure Microhardness Long period stacking ordered phase Intermetallic phase zn-y alloys period ordered structure mechanical-properties magnesium alloy solid-solution strength behavior system phase re
ISSN号	0925-8388
中文摘要	The microstructures and the corresponding microhardness evolution of a Mg(83)Ni(6)Zn(5)Y(6) (at.%) alloy subjected to a series of heat treatments were investigated. In addition to the 14H long period stacking ordered (LPSO) phase, a diamond-cubic phase with the possible space group of Fd (3) over barm and lattice parameter of a = 0.73nm were identified in the as-cast alloy. The combination of LPSO thin lamellae and the nanometer-sized cubic phase leads to a relatively high Vickers microhardness of about 116.2 +/- 13.7. When annealed at 473K and 573 K, the above diamond-cubic phase partially transforms to its structural variant, Fm (3) over barm, together with a slight change of lattice parameter (a = 0.72 nm). Precipitation of hexagonal Mg(2)Ni lath also happens at these moderate annealing temperatures. The remarkable increase of microhardness at this stage is believed to result from the strengthening of precipitates and the resultant coherent interface between the precipitates and their surrounding medium. When annealed at temperatures ranging from 673K to 773 K, the Mg(2)Ni precipitates were dissolved, grain coarsening in the alloy occurred, Fd (3) over barm phase completely transformed to its Fm (3) over barm counterpart, and consequently microhardness of the alloy was decreased significantly. (C) 2011 Elsevier B. V. All rights reserved.
原文出处	://WOS:000291005700007
公开日期	2012-04-13
内容类型	期刊论文
源URL	[http://210.72.142.130/handle/321006/30647]
专题	金属研究所_中国科学院金属研究所
推荐引用方式 GB/T 7714	X. H. Shao,Z. Q. Yang,J. H. You,et al. Microstructure and microhardness evolution of a Mg(83)Ni(6)Zn(5)Y(6) alloy upon annealing[J]. Journal of Alloys and Compounds,2011,509(26):7221-7228.
APA	X. H. Shao,Z. Q. Yang,J. H. You,K. Q. Qiu,&X. L. Ma.(2011).Microstructure and microhardness evolution of a Mg(83)Ni(6)Zn(5)Y(6) alloy upon annealing.Journal of Alloys and Compounds,509(26),7221-7228.
MLA	X. H. Shao,et al."Microstructure and microhardness evolution of a Mg(83)Ni(6)Zn(5)Y(6) alloy upon annealing".Journal of Alloys and Compounds 509.26(2011):7221-7228.