Annealing behavior of Ag nanoparticles in silica with and without defects | |
Yang, Yitao1![]() | |
刊名 | VACUUM
![]() |
2016-07-01 | |
卷号 | 129页码:130-134 |
关键词 | Defects Ag nanoparticles Silica Surface plasmon resonance Annealing behavior |
ISSN号 | 0042-207X |
DOI | 10.1016/j.vacuum.2016.04.023 |
英文摘要 | In this paper we investigated the annealing behavior of Ag nanoparticles in silica with and without defects. Silica samples with and without Ar ion pre-irradiation were implanted with Ag ions and then annealed at temperature from 300 to 850 degrees C. UV-VIS spectroscopy and TEM were used to characterize the optical absorbance property and size distribution of Ag nanoparticles, respectively. Optical absorbance results showed that the absorbance intensity of SPR peak from Ag nanoparticles in the sample with pre-irradiation was stronger than in the sample without pre-irradiation. During annealing, compared to the sample without pre-irradiation, the normalized absorbance intensity of SPR peak fluctuated in a smaller range with temperature for the sample with pre-irradiation. This indicated that defects produced by pre-irradiation prevented Ag nanoparticles from a rapid growth during annealing, namely had a stabilizing effect on Ag nanoparticles. However, in contrast to the sample without pre-irradiation, the SPR peak started to became broad and weak at a relative low temperature and fully disappeared after annealing at 850 degrees C for the sample with pre-irradiation. This indicated that defects could accelerate the decomposition of Ag nanoparticles at higher temperature. (C) 2016 Elsevier Ltd. All rights reserved. |
资助项目 | National Natural Science Foundation of China (NSFC)[11475230] ; National Natural Science Foundation of China (NSFC)[11005132] |
WOS关键词 | ION-IMPLANTATION ; SILVER NANOPARTICLES ; GOLD NANOCLUSTERS ; IRRADIATION ; GLASS ; NUCLEATION ; SPINEL ; SIZE ; CU |
WOS研究方向 | Materials Science ; Physics |
语种 | 英语 |
出版者 | PERGAMON-ELSEVIER SCIENCE LTD |
WOS记录号 | WOS:000377313500021 |
资助机构 | National Natural Science Foundation of China (NSFC) |
内容类型 | 期刊论文 |
源URL | [http://119.78.100.186/handle/113462/24418] ![]() |
专题 | 近代物理研究所_材料研究中心 |
通讯作者 | Yang, Yitao |
作者单位 | 1.Chinese Acad Sci, Inst Modem Phys, Lanzhou 730000, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Yang, Yitao,Yan, Tingxing,Song, Yin,et al. Annealing behavior of Ag nanoparticles in silica with and without defects[J]. VACUUM,2016,129:130-134. |
APA | Yang, Yitao,Yan, Tingxing,Song, Yin,Gou, Jie,&Zhang, Chonghong.(2016).Annealing behavior of Ag nanoparticles in silica with and without defects.VACUUM,129,130-134. |
MLA | Yang, Yitao,et al."Annealing behavior of Ag nanoparticles in silica with and without defects".VACUUM 129(2016):130-134. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论