Characterization of the strain in the thermal barrier coatings caused by molten CaO-MgO-Al2O3-SiO2 using a digital image correlation technique | |
Yang, L. ; Yang, J. ; Xia, J. ; Zhu, W. ; Zhou, Y. C. ; Wei, Y. G. ; Wu, R. T. | |
刊名 | SURFACE & COATINGS TECHNOLOGY |
2017 | |
关键词 | Thermal barrier coatings High temperature corrosion CaO-MgO-Al2O3-SiO2 Digital image correlation HIGH-TEMPERATURE ATTACK TBC SYSTEM FAILURE CMAS DEPOSITS STRESS-DISTRIBUTION GLASSY DEPOSITS MECHANISMS DEGRADATION DELAMINATION INFILTRATION RESISTANCE |
DOI | 10.1016/j.surfcoat.2017.05.025 |
英文摘要 | The strain field of the thermal barrier coatings (TBCs) corroded by molten CaO-MgO-Al2O3-SiO2 (CMAS) is investigated using the digital image correlation (DIC) techniques. The results indicate that the strain in TBCs is compressive and it increases during cooling from 1250 to 25 degrees C. The cracks induced by CMAS form at the YSZ/BC interface at 300-400 degrees C. These cracks can be observed even without CMAS as temperature decreases to 100 degrees C. The DIC measurements show that the critical strains for the failure of TBCs with and without CMAS are 0.7% and -1.6%, respectively, and these results can be predicted by using a theoretical model. (C) 2017 Elsevier B.V. All rights reserved.; National Natural Science Foundation of China [51590891, 11472237, 11602211, 11432014]; Distinguished Young Scholar Foundation of Hunan Province [2016JJ1014]; Outstanding Youth Foundation of Hunan Provincial Education Department [168249]; SCI(E); ARTICLE; 1-9; 322 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/471489] |
专题 | 工学院 |
推荐引用方式 GB/T 7714 | Yang, L.,Yang, J.,Xia, J.,et al. Characterization of the strain in the thermal barrier coatings caused by molten CaO-MgO-Al2O3-SiO2 using a digital image correlation technique[J]. SURFACE & COATINGS TECHNOLOGY,2017. |
APA | Yang, L..,Yang, J..,Xia, J..,Zhu, W..,Zhou, Y. C..,...&Wu, R. T..(2017).Characterization of the strain in the thermal barrier coatings caused by molten CaO-MgO-Al2O3-SiO2 using a digital image correlation technique.SURFACE & COATINGS TECHNOLOGY. |
MLA | Yang, L.,et al."Characterization of the strain in the thermal barrier coatings caused by molten CaO-MgO-Al2O3-SiO2 using a digital image correlation technique".SURFACE & COATINGS TECHNOLOGY (2017). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论