Hydrogen adsorption of open-tipped insufficiently graphitized   multiwalled carbon nanotubes

doi:10.1063/1.1620675

CORC > 北京大学 > 化学与分子工程学院

	Hydrogen adsorption of open-tipped insufficiently graphitized multiwalled carbon nanotubes
	Gao, H ; Wu, XB ; Li, JT ; Wu, GT ; Lin, JY ; Wu, K ; Xu, DS
刊名	应用物理学快报
	2003
关键词	STORAGE CAPACITY ACTIVATED CARBONS ROOM-TEMPERATURE AREA
DOI	10.1063/1.1620675
英文摘要	Open-tipped carbon nanotubes with a large amount of subnanopores and open ends on the tube wall were conveniently prepared by an improved anodized aluminum oxide template growth. The hydrogen storage was measured based on a volumetric method. Adsorptions of 6.46 and 1.12 wt % were achieved at 77 K and room temperature, respectively. Compared to hydrogen adsorption of other carbon materials, rough wall surface, opening tips, subnanopores, and opening ends on the wall were attributed to greatly enhanced hydrogen storage. (C) 2003 American Institute of Physics.; Physics, Applied; SCI(E); EI; 0; ARTICLE; 16; 3389-3391; 83
语种	英语
内容类型	期刊论文
源URL	[http://ir.pku.edu.cn/handle/20.500.11897/255628]
专题	化学与分子工程学院
推荐引用方式 GB/T 7714	Gao, H,Wu, XB,Li, JT,et al. Hydrogen adsorption of open-tipped insufficiently graphitized multiwalled carbon nanotubes[J]. 应用物理学快报,2003.
APA	Gao, H.,Wu, XB.,Li, JT.,Wu, GT.,Lin, JY.,...&Xu, DS.(2003).Hydrogen adsorption of open-tipped insufficiently graphitized multiwalled carbon nanotubes.应用物理学快报.
MLA	Gao, H,et al."Hydrogen adsorption of open-tipped insufficiently graphitized multiwalled carbon nanotubes".应用物理学快报 (2003).