Crystalline behaviors and phase transition during the manufacture of fine denier PA6 fibers | |
Zhang ChengFeng ; Liu YuHai ; Liu ShaoXuan ; Li HuiZhen ; Huang Kun ; Pan QingHua ; Hua XiaoHui ; Hao ChaoWei ; Ma QingFang ; Lv ChangYou ; Li WeiHong ; Yang ZhanLan ; Zhao Ying ; Wang DuJin ; Lai GuoQiao ; Jiang JianXiong ; Xu YiZhuang ; Wu JinGuang | |
刊名 | 中国科学b辑 化学英文版 |
2009 | |
关键词 | nylon 6 fiber crystallization FT-IR XRD X-RAY-DIFFRACTION NYLON 6 GAMMA-FORM STRUCTURAL-CHANGES LITHIUM-SALTS ALPHA-FORM POLYAMIDE POLYMERS POLYCAPROAMIDE COMPLEXATION |
DOI | 10.1007/s11426-009-0242-5 |
英文摘要 | Recently we have successfully produced fine denier PA6 fibers by using additives containing lanthanide compounds. Meanwhile, crystallization and phase transition of PA6 fibers during spinning and drawing processes were investigated. During the spinning process, beta phase crystal could be obtained in as-spun PA6 fibers which were produced with relatively high melt draw ratio, while gamma phase crystal predominated when the melt draw ratio was relatively low. beta phase crystal, whose behaviors are similar with those of gamma phase by FT-IR and XRD characterization, could be transformed to alpha form easily when PA6 fibers are immersed in boiling water. However, gamma phase crystal of PA6 remains unchanged in boiling water. Thus, beta and gamma phase crystals of PA6 can be differentiated by the crystalline behaviors of PA6 fibers after treatment in boiling water. Further experiments demonstrate that the beta phase can also be produced during a drawing process where a phase transformation from gamma to alpha occurs. In other words, beta phase may act as an intermediate state during the phase transformation.; http://gateway.webofknowledge.com/gateway/Gateway.cgi?GWVersion=2&SrcApp=PARTNER_APP&SrcAuth=LinksAMR&KeyUT=WOS:000272032700014&DestLinkType=FullRecord&DestApp=ALL_WOS&UsrCustomerID=8e1609b174ce4e31116a60747a720701 ; Chemistry, Multidisciplinary; SCI(E); EI; 10; ARTICLE; 11; 1835-1842; 52 |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.pku.edu.cn/handle/20.500.11897/245308] |
专题 | 化学与分子工程学院 |
推荐引用方式 GB/T 7714 | Zhang ChengFeng,Liu YuHai,Liu ShaoXuan,et al. Crystalline behaviors and phase transition during the manufacture of fine denier PA6 fibers[J]. 中国科学b辑 化学英文版,2009. |
APA | Zhang ChengFeng.,Liu YuHai.,Liu ShaoXuan.,Li HuiZhen.,Huang Kun.,...&Wu JinGuang.(2009).Crystalline behaviors and phase transition during the manufacture of fine denier PA6 fibers.中国科学b辑 化学英文版. |
MLA | Zhang ChengFeng,et al."Crystalline behaviors and phase transition during the manufacture of fine denier PA6 fibers".中国科学b辑 化学英文版 (2009). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论