	Cold spraying SiC/Al metal matrix composites: effects of SiC contents and heat treatment on microstructure, thermophysical and flexural properties
	Gyansah, L; Tariq, NH; Tang, JR; Qiu, X; Feng, B; Huang, J; Du, H; Wang, JQ; Xiong, TY; Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
刊名	MATERIALS RESEARCH EXPRESS
	2018-02-01
卷号	5期号:2页码:-
关键词	Laminated Zrb2-sic/graphite Ceramics Mechanical-properties Coatings Behavior Al Aluminum Tin Microhardness Powder Copper
ISSN号	2053-1591
英文摘要	In this paper, cold spray was used as an additive manufacturing method to fabricate 5mmthick SiC/Al metal matrix composites with various SiC contents. The effects of SiC contents and heat treatment on the microstructure, thermophysical and flexural properties were investigated. Additionally, the composites were characterized for retention of SiC particulates, splat size, surface roughness and the progressive understanding of strengthening, toughening and cracking mechanisms. Mechanical properties were investigated via three-point bending test, thermophysical analysis, and hardness test. In the as-sprayed state, flexural strength increased from 95.3 MPa to 133.5 MPa, an appreciation of 40% as the SiC contents increased, and the main toughening and strengthening mechanisms were zigzag crack propagation and high retention of SiC particulates respectively. In the heat treatment conditions, flexural strength appreciated significantly compared to the as-sprayed condition and this was as a result of coarsening of pure Al splat. Crack branching, crack deflection and interface delamination were considered as the main toughening mechanisms at the heat treatment conditions. Experimental results were consistent with the measured CTE, hardness, porosity and flexural modulus.; In this paper, cold spray was used as an additive manufacturing method to fabricate 5mmthick SiC/Al metal matrix composites with various SiC contents. The effects of SiC contents and heat treatment on the microstructure, thermophysical and flexural properties were investigated. Additionally, the composites were characterized for retention of SiC particulates, splat size, surface roughness and the progressive understanding of strengthening, toughening and cracking mechanisms. Mechanical properties were investigated via three-point bending test, thermophysical analysis, and hardness test. In the as-sprayed state, flexural strength increased from 95.3 MPa to 133.5 MPa, an appreciation of 40% as the SiC contents increased, and the main toughening and strengthening mechanisms were zigzag crack propagation and high retention of SiC particulates respectively. In the heat treatment conditions, flexural strength appreciated significantly compared to the as-sprayed condition and this was as a result of coarsening of pure Al splat. Crack branching, crack deflection and interface delamination were considered as the main toughening mechanisms at the heat treatment conditions. Experimental results were consistent with the measured CTE, hardness, porosity and flexural modulus.
学科主题	Materials Science, Multidisciplinary
语种	英语
资助机构	National Natural Science Foundation of China [51671205]
公开日期	2018-06-05
内容类型	期刊论文
源URL	[http://ir.imr.ac.cn/handle/321006/79538]
专题	金属研究所_中国科学院金属研究所
通讯作者	Wang, JQ (reprint author), Chinese Acad Sci, Inst Met Res, Shenyang 110016, Liaoning, Peoples R China.
推荐引用方式 GB/T 7714	Gyansah, L,Tariq, NH,Tang, JR,et al. Cold spraying SiC/Al metal matrix composites: effects of SiC contents and heat treatment on microstructure, thermophysical and flexural properties[J]. MATERIALS RESEARCH EXPRESS,2018,5(2):-.
APA	Gyansah, L.,Tariq, NH.,Tang, JR.,Qiu, X.,Feng, B.,...&Wang, JQ .(2018).Cold spraying SiC/Al metal matrix composites: effects of SiC contents and heat treatment on microstructure, thermophysical and flexural properties.MATERIALS RESEARCH EXPRESS,5(2),-.
MLA	Gyansah, L,et al."Cold spraying SiC/Al metal matrix composites: effects of SiC contents and heat treatment on microstructure, thermophysical and flexural properties".MATERIALS RESEARCH EXPRESS 5.2(2018):-.

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。