Preparation and photoluminescence of water-dispersible ZnSe nanocrystals | |
Murase, N; Gao, MY | |
刊名 | MATERIALS LETTERS |
2004-12-01 | |
卷号 | 58期号:30页码:3898-3902 |
关键词 | Photoluminescence Excitonic Emission Znse Nanocrystals |
ISSN号 | 0167-577X |
DOI | 10.1016/j.matlet.2004.03.055 |
英文摘要 | Water-dispersible ZnSe nanocrystals (2-3 run in diameter) producing photoluminescence (PL) in a blue region were prepared using several thiol-stabilizers. Thioglycerol (TG) gives the most intense PL having a shoulder at 387 run and a maximum at 475 nm, The former was assigned to the excitonic emission, whereas the latter was assigned to a defect emission. Reflux increases the PL intensity, but did not change its peak wavelength significantly. TG plays an essential role in stabilizing the ZnSe colloidal solution, but it also creates defect emission. Therefore, the less the amount of surfactant, the more the PL intensity becomes in a range where the solution is not precipitated. The attachment and removal of TG on the surface of nanocrystals only occur at refluxing temperature (100 degreesC). On the other hand, removal of hydroxyl ions from the surface occurs at room temperature when pH is reduced. The zeta-potential and PL intensity are correlated strongly with the pH of the colloidal solution. This indicates hydroxyl ions passivate the surface significantly. Under optimized conditions of TG ratio and reflux time, the ZnSe nanocrystals in water produced whitish-blue emissions with an efficiency of 10% relative to rhodamine 6G. The nanocrystals in water are stable for months in a refrigerator. (C) 2004 Elsevier B.V. All rights reserved. |
语种 | 英语 |
出版者 | ELSEVIER SCIENCE BV |
WOS记录号 | WOS:000224947900014 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/81719] |
专题 | 中国科学院化学研究所 |
通讯作者 | Murase, N |
作者单位 | 1.Natl Inst AIST, Ikeda, Osaka 5638577, Japan 2.Chinese Acad Sci, Inst Chem, Beijing 100080, Peoples R China |
推荐引用方式 GB/T 7714 | Murase, N,Gao, MY. Preparation and photoluminescence of water-dispersible ZnSe nanocrystals[J]. MATERIALS LETTERS,2004,58(30):3898-3902. |
APA | Murase, N,&Gao, MY.(2004).Preparation and photoluminescence of water-dispersible ZnSe nanocrystals.MATERIALS LETTERS,58(30),3898-3902. |
MLA | Murase, N,et al."Preparation and photoluminescence of water-dispersible ZnSe nanocrystals".MATERIALS LETTERS 58.30(2004):3898-3902. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论