	Nanocrystalline silicon films with high conductivity and the application for pin solar cells
	Cui Min; Zhang Weija; Wang Tianmin; Jin Fei; Li Guohua; Ding Kun
刊名	Vacuum
	2006-09-16
卷号	81期号:1页码:126-128
关键词	Nc-si : h Conductivity Pecvd Films Solar cells
ISSN号	0042-207X
DOI	10.1016/j.vacuum.2005.12.006
通讯作者	Cui min(xinzhu_hust@126.com)
英文摘要	Intrinsic nanocrystalline silicon films (nc-si:h) were prepared by plasma enhanced chemical vapor deposition (pecvd) method. films' microstructures and characteristics were studied with raman spectroscopy and atom force microscope (afm). the electronic conductivity of nc-si:h films was found to be 4.9 x 10(0)omega(-1) cm(-1), which was one order of magnitude higher than the reported 10(-3)-10(-1)omega(-1)cm(-1). and pin solar cells with nc-si:h film as intrinsic thin-layer (ito/n(+)-nc-si:h/i-nc-si:h/p-c-si/ag) were researched. the cell's performances were measured, the open-circuit voltage v-oc was 534.7 mv, short-circuit current i-sc was 49.24 ma (3 cm(2)) and fill factor ff was 0.4228. (c) 2006 elsevier ltd. all rights reserved.
WOS研究方向	Materials Science ; Physics
WOS类目	Materials Science, Multidisciplinary ; Physics, Applied
语种	英语
出版者	PERGAMON-ELSEVIER SCIENCE LTD
WOS记录号	WOS:000240582100022
内容类型	期刊论文
URI标识	http://www.corc.org.cn/handle/1471x/2426628
专题	半导体研究所
通讯作者	Cui Min
作者单位	1.Beihang Univ, Sch Sci, Ctr Condensed Phys & Mat Phys, Beijing 100083, Peoples R China 2.Chinese Acad Sci, Inst Semicond, Natl Lab Superlattices & Microstruct, Beijing 100083, Peoples R China
推荐引用方式 GB/T 7714	Cui Min,Zhang Weija,Wang Tianmin,et al. Nanocrystalline silicon films with high conductivity and the application for pin solar cells[J]. Vacuum,2006,81(1):126-128.
APA	Cui Min,Zhang Weija,Wang Tianmin,Jin Fei,Li Guohua,&Ding Kun.(2006).Nanocrystalline silicon films with high conductivity and the application for pin solar cells.Vacuum,81(1),126-128.
MLA	Cui Min,et al."Nanocrystalline silicon films with high conductivity and the application for pin solar cells".Vacuum 81.1(2006):126-128.

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。