Structure and micromorphology of wear debris of mc nylon 6 under dry sliding: correlation with wear mechanisms | |
Ning, Liping1,2; Jian, Lingqi1,2; Wang, Jinqing1; Yang, Shengrong1; Wang, Jianmin1 | |
刊名 | Tribology transactions
![]() |
2009 | |
卷号 | 52期号:6页码:793-799 |
关键词 | Mc nylon 6 Wear debris Structure Micromorphology Wear mechanisms |
ISSN号 | 1040-2004 |
DOI | 10.1080/10402000903097494 |
通讯作者 | Ning, liping() |
英文摘要 | The structure and micromorphology of wear debris of mc nylon 6 under dry sliding were investigated by ftir, xrd, dsc, and fesem, and the 3d surface topographies of friction materials before and after the friction test were observed, which will be helpful in understanding the friction and wear processes. the primary crystalline phase of both the unworn mc nylon 6 and the wear debris were crystal, but the crystallinity of the latter was higher than that of the former. the proportion of 2(002 + 202) planes increased and the reflection from the 1(200) planes was suppressed in the wear debris, indicating a preferential arrangement of 2(002 + 202) on the surface of the wear debris. the transition in structure of the wear debris originated from the activation of the chain segments due to the thermodynamic effects. the thermodynamic effects and high chain segment mobility resulted in the hydrogen bonding whose interchain distance is a larger rupture or even chain scission. mc nylon 6 was severely worn due to the contribution of the tearing force that resulted from the combined action of the tribo-interface adhesion and the shearing effect during friction, whereas no damage happened on the worn surface of the counterpart steel pin even if under severe sliding conditions. |
WOS关键词 | BEHAVIOR ; CRYSTALLIZATION ; POLYETHYLENE ; TRANSITION ; UHMWPE |
WOS研究方向 | Engineering |
WOS类目 | Engineering, Mechanical |
语种 | 英语 |
出版者 | TAYLOR & FRANCIS INC |
WOS记录号 | WOS:000272211900009 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2396634 |
专题 | 中国科学院大学 |
通讯作者 | Ning, Liping |
作者单位 | 1.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Ning, Liping,Jian, Lingqi,Wang, Jinqing,et al. Structure and micromorphology of wear debris of mc nylon 6 under dry sliding: correlation with wear mechanisms[J]. Tribology transactions,2009,52(6):793-799. |
APA | Ning, Liping,Jian, Lingqi,Wang, Jinqing,Yang, Shengrong,&Wang, Jianmin.(2009).Structure and micromorphology of wear debris of mc nylon 6 under dry sliding: correlation with wear mechanisms.Tribology transactions,52(6),793-799. |
MLA | Ning, Liping,et al."Structure and micromorphology of wear debris of mc nylon 6 under dry sliding: correlation with wear mechanisms".Tribology transactions 52.6(2009):793-799. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论