Uv-curable waterborne polyurethane from co2-polyol with high hydrolysis resistance | |
Wang, Jin1,2; Zhang, Hongming1; Miao, Yuyang1; Qiao, Lijun1; Wang, Xianhong1; Wang, Fosong1 | |
刊名 | Polymer |
2016-09-25 | |
卷号 | 100页码:219-226 |
关键词 | Carbon dioxide Uv-curable waterborne polyurethane Hydrolysis resistance |
ISSN号 | 0032-3861 |
DOI | 10.1016/j.polymer.2016.08.039 |
通讯作者 | Zhang, hongming(hmzhang@ciac.ac.cn) ; Wang, xianhong(xhwang@ciac.ac.cn) |
英文摘要 | Uv-curable waterborne polyurethanes (co2-uv-wpus) with co2-polyols as soft segment were firstly synthesized. in addition to the good mechanical performance, the coexistence of carbonate and ether moieties in soft segment assured the excellent hydrolysis resistance of co2-uv-wpu compared with polybutylene adipate glycol based waterborne polyurethane (pba-uv-wpu). its retention of tensile strength reached 88% after 15 h immersion in 1.5% sodium hydroxide solution, while that of pba-uv-wpu completely lost its mechanical property. the double bond density primarily governed the mechanical performance of co2-uv-wpu, when it increased from 0.93 mmol/g to 2.4 mmol/g, the tensile strength increased from 29 mpa to 67 mpa, while elongation at break decreased from 150% to 9.6%, accompanied by the reduction of maximum water swelling percentage from 26.7% to 14.5%. the introduction of co2-polyol as soft segment not only created a route to produce uv-curable waterborne polyurethane from co2, but also provided polyurethane with novel value-added performance like good hydrolysis resistance. moreover, the thermal/mechanical performance and hydrophilicity of co2-uv-wpus could be conveniently adjusted by controlling molecular weight of co2-polyols, ensuring the application feasibility of co2-uv-wpu. (c) 2016 elsevier ltd. all rights reserved. |
WOS关键词 | CARBON-DIOXIDE ; OLIGO(CARBONATE-ETHER) DIOLS ; MOLECULAR-WEIGHT ; CHAIN EXTENSION ; CROSS-LINKING ; DISPERSIONS ; COPOLYMERIZATION ; CO2 ; ELASTOMERS ; COATINGS |
WOS研究方向 | Polymer Science |
WOS类目 | Polymer Science |
语种 | 英语 |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000383925800026 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2376076 |
专题 | 中国科学院大学 |
通讯作者 | Zhang, Hongming; Wang, Xianhong |
作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, Key Lab Polymer Ecomat, Changchun 130022, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100039, Peoples R China |
推荐引用方式 GB/T 7714 | Wang, Jin,Zhang, Hongming,Miao, Yuyang,et al. Uv-curable waterborne polyurethane from co2-polyol with high hydrolysis resistance[J]. Polymer,2016,100:219-226. |
APA | Wang, Jin,Zhang, Hongming,Miao, Yuyang,Qiao, Lijun,Wang, Xianhong,&Wang, Fosong.(2016).Uv-curable waterborne polyurethane from co2-polyol with high hydrolysis resistance.Polymer,100,219-226. |
MLA | Wang, Jin,et al."Uv-curable waterborne polyurethane from co2-polyol with high hydrolysis resistance".Polymer 100(2016):219-226. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论