Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel with Sulfate-Reducing Bacteria | |
Zhang Jie1; Li Xiaolong1,2; Wang Jiangwei1; Xu Weichen1; Duan Jizhou1; Chen Shougang3; Hou Baorong1 | |
刊名 | JOURNAL OF OCEAN UNIVERSITY OF CHINA |
2017-12-01 | |
卷号 | 16期号:6页码:1213-1219 |
关键词 | Microbiological Corrosion Sulfate-reducing Bacteria Calcareous Deposit Cathodic Protection |
DOI | 10.1007/s11802-017-3266-z |
文献子类 | Article |
英文摘要 | Cathodic protection is a very effective method to protect metals, which can form calcareous deposits on metal surface. Research on the interrelationship between fouling organism and calcareous deposits is very important but very limited, especially sulfate-reducing bacteria (SRB). SRB is a kind of very important fouling organism that causes microbial corrosion of metals. A study of the influence of calcareous deposit on corrosion behavior of Q235 carbon steel in SRB-containing culture medium was carried out using electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM) and surface spectroscopy (EDS). The calcareous deposit was formed with good crystallinity and smooth surface under the gradient current density of -30 mu A cm(-2) in natural seawater for 72 h. Our results can help elucidate the formation of calcareous deposits and reveal the interrelationship between SRB and calcareous deposits under cathodic protection. The results indicate that the corrosion tendency of carbon steel was obviously affected by Sulfate-reducing Bacteria (SRB) metabolic activity and the calcareous deposit formed on the surface of carbon steel under cathodic protection was favourable to reduce the corrosion rate. Calcareous deposits can promote bacterial adhesion before biofilm formation. The results revealed the interaction between biofouling and calcareous deposits, and the anti-corrosion ability was enhanced by a kind of inorganic and organic composite membranes formed by biofilm and calcareous deposits. |
语种 | 英语 |
WOS记录号 | WOS:000414791700033 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.qdio.ac.cn/handle/337002/143044] |
专题 | 海洋研究所_实验海洋生物学重点实验室 海洋研究所_海洋腐蚀与防护研究发展中心 |
作者单位 | 1.Chinese Acad Sci, Key Lab Marine Environm Corros & Biofouling, Inst Oceanol, Qingdao 266071, Peoples R China 2.Univ Chinese Acad Sci, Beijing 10049, Peoples R China 3.Ocean Univ China, Inst Mat Sci & Engn, Qingdao 266100, Peoples R China |
推荐引用方式 GB/T 7714 | Zhang Jie,Li Xiaolong,Wang Jiangwei,et al. Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel with Sulfate-Reducing Bacteria[J]. JOURNAL OF OCEAN UNIVERSITY OF CHINA,2017,16(6):1213-1219. |
APA | Zhang Jie.,Li Xiaolong.,Wang Jiangwei.,Xu Weichen.,Duan Jizhou.,...&Hou Baorong.(2017).Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel with Sulfate-Reducing Bacteria.JOURNAL OF OCEAN UNIVERSITY OF CHINA,16(6),1213-1219. |
MLA | Zhang Jie,et al."Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel with Sulfate-Reducing Bacteria".JOURNAL OF OCEAN UNIVERSITY OF CHINA 16.6(2017):1213-1219. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论