The highly twinned grain boundary network formation during grain boundary engineering | |
Liu, Tingguang[1]; Xia, Shuang[2]; Li, Hui[3]; Zhou, Bangxin[4]; Bai, Qin[5] | |
刊名 | MATERIALS LETTERS |
2014 | |
卷号 | 133页码:97-100 |
关键词 | Grain boundary Recrystallization Grain boundary engineering Twinning Grain-cluster |
ISSN号 | 0167-577X |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2280971 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Univ, Inst Mat, Shanghai 200072, Peoples R China. 2.[2]Shanghai Univ, Inst Mat, Shanghai 200072, Peoples R China. 3.Shanghai Univ, Key Lab Microstruct, Shanghai 200444, Peoples R China. 4.[3]Shanghai Univ, Key Lab Microstruct, Shanghai 200444, Peoples R China. 5.[4]Shanghai Univ, Inst Mat, Shanghai 200072, Peoples R China. 6.Shanghai Univ, Key Lab Microstruct, Shanghai 200444, Peoples R China. 7.[5]Shanghai Univ, Key Lab Microstruct, Shanghai 200444, Peoples R China. |
推荐引用方式 GB/T 7714 | Liu, Tingguang[1],Xia, Shuang[2],Li, Hui[3],et al. The highly twinned grain boundary network formation during grain boundary engineering[J]. MATERIALS LETTERS,2014,133:97-100. |
APA | Liu, Tingguang[1],Xia, Shuang[2],Li, Hui[3],Zhou, Bangxin[4],&Bai, Qin[5].(2014).The highly twinned grain boundary network formation during grain boundary engineering.MATERIALS LETTERS,133,97-100. |
MLA | Liu, Tingguang[1],et al."The highly twinned grain boundary network formation during grain boundary engineering".MATERIALS LETTERS 133(2014):97-100. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论