Analysis of the oxidized surface of 90Nb-10Zr alloy after exposure to lithiated water with 0.01 M LiOH at 360 degrees C/18.6 MPa | |
Huang, J.[1]; Yao, M. Y.[2]; Gao, C. Y.[3]; Hu, P. F.[4]; Liang, X.[5]; Zhang, J. L.[6]; Zhou, B. X.[7]; Li, Q.[8]; Ahsan, E.[9] | |
刊名 | CORROSION SCIENCE |
2016 | |
卷号 | 104页码:269-276 |
关键词 | Zirconium TEM High temperature corrosion Oxidation |
ISSN号 | 0010-938X |
URL标识 | 查看原文 |
内容类型 | 期刊论文 |
URI标识 | http://www.corc.org.cn/handle/1471x/2235756 |
专题 | 上海大学 |
作者单位 | 1.[1]Shanghai Univ, Inst Mat, POB 269,149 Yanchang Rd, Shanghai 200072, Peoples R China. 2.Shanghai Univ, Lab Microstruct, Shanghai 200444, Peoples R China. 3.[2]Shanghai Univ, Inst Mat, POB 269,149 Yanchang Rd, Shanghai 200072, Peoples R China. 4.Shanghai Univ, Lab Microstruct, Shanghai 200444, Peoples R China. 5.[3]Shanghai Univ, Inst Mat, POB 269,149 Yanchang Rd, Shanghai 200072, Peoples R China. 6.Shanghai Univ, Lab Microstruct, Shanghai 200444, Peoples R China. 7.[4]Shanghai Univ, Inst Mat, POB 269,149 Yanchang Rd, Shanghai 200072, Peoples R China. 8.Shanghai Univ, Lab Microstruct, Shanghai 200444, Peoples R China. 9.[5]Shanghai Univ, Inst Mat, POB 269,149 Yanchang Rd, Shanghai 200072, Peoples R China. 10.Shanghai Univ, Lab Microstruct, Shanghai 200444, Peoples R China. |
推荐引用方式 GB/T 7714 | Huang, J.[1],Yao, M. Y.[2],Gao, C. Y.[3],et al. Analysis of the oxidized surface of 90Nb-10Zr alloy after exposure to lithiated water with 0.01 M LiOH at 360 degrees C/18.6 MPa[J]. CORROSION SCIENCE,2016,104:269-276. |
APA | Huang, J.[1].,Yao, M. Y.[2].,Gao, C. Y.[3].,Hu, P. F.[4].,Liang, X.[5].,...&Ahsan, E.[9].(2016).Analysis of the oxidized surface of 90Nb-10Zr alloy after exposure to lithiated water with 0.01 M LiOH at 360 degrees C/18.6 MPa.CORROSION SCIENCE,104,269-276. |
MLA | Huang, J.[1],et al."Analysis of the oxidized surface of 90Nb-10Zr alloy after exposure to lithiated water with 0.01 M LiOH at 360 degrees C/18.6 MPa".CORROSION SCIENCE 104(2016):269-276. |