On failure modes and strength characterization of brittle disordered materials under uniaxial compression and tension | |
Tang CA(唐春安); Lin P; Liu HY(刘红元) | |
刊名 | Key Engineering Materials |
2000 | |
卷号 | 183-187期号:Fracture and Strength of Solids IV页码:637-642 |
ISSN号 | 1013-9826 |
通讯作者 | Tang, CA (reprint author), Northeastern Univ, Resources & Civil Engn Sch, CRISR, Shenyang 110006, Peoples R China. |
合作状况 | 国内 |
中文摘要 | With a newly developed Material Failure Process Analysis code (MFPA(2D)), influence of hetero geneity on fracture processes and strength characterization of brittle disorder materials such as rock or concrete is numerically studied under uniaxial compression and tension conditions. It is found th at, due to the heterogeneity of the disordered material, relatively more diffused micro-fractures appear in the early stage of loading. Different from homogeneous materials such as glass, macro-crack nucleation starts well before the peak stress is reached and the crack propagation and coalescence can be traced, which can be taken as a precursory to predict the macro-fracture of the material. The presence of residual strength in the post-peak region and the resemblance in the stress-strain curves between tension and compression are significant results and are found to be dependent on the heterogeneity of the specimens. Examples showing the tentative applications of MFPA(2D) in modeling failure of composite materials and rock or civil engineering problem are also given in this paper. |
学科主题 | 力学 |
类目[WOS] | Materials Science, Ceramics ; Mechanics ; Materials Science, Characterization & Testing ; Materials Science, Composites |
研究领域[WOS] | Materials Science ; Mechanics |
收录类别 | SCI ; EI |
原文出处 | http://www.scientific.net/KEM.183-187.637 |
语种 | 英语 |
WOS记录号 | WOS:000165527800105 |
公开日期 | 2007-06-15 ; 2007-12-05 ; 2009-06-23 |
内容类型 | 期刊论文 |
源URL | [http://dspace.imech.ac.cn/handle/311007/17421] |
专题 | 力学研究所_力学所知识产出(1956-2008) |
推荐引用方式 GB/T 7714 | Tang CA,Lin P,Liu HY. On failure modes and strength characterization of brittle disordered materials under uniaxial compression and tension[J]. Key Engineering Materials,2000,183-187(Fracture and Strength of Solids IV):637-642. |
APA | Tang CA,Lin P,&Liu HY.(2000).On failure modes and strength characterization of brittle disordered materials under uniaxial compression and tension.Key Engineering Materials,183-187(Fracture and Strength of Solids IV),637-642. |
MLA | Tang CA,et al."On failure modes and strength characterization of brittle disordered materials under uniaxial compression and tension".Key Engineering Materials 183-187.Fracture and Strength of Solids IV(2000):637-642. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论