Enhanced mechanical property of Ca-5(PO4)(2)SiO4 bioceramic by a biocompatible sintering aid of zinc oxide | |
Deng, Fanyan2; Wang, Feng; Liu, Ziwei1; Kou, Huamin; Cheng, Guofeng1; Ning, Congqin | |
刊名 | CERAMICS INTERNATIONAL |
2018 | |
卷号 | 44期号:15页码:18352 |
关键词 | Calcium phosphate silicate Zinc oxide Bioceramic Sintering aid Mechanical property |
ISSN号 | 0272-8842 |
DOI | 10.1016/j.ceramint.2018.07.051 |
英文摘要 | In the present work, a biocompatible additive ZnO was used to enhance the sintering of calcium phosphate silicate (CPS)(1) bioceramic and improve its mechanical property. Sol-gel prepared CPS powders were mechanically mixed with various amount of ZnO and then sintered at high temperatures to prepare Zn-CPS bioceramics. The effects of ZnO content and sintering temperature on microstructure and bending strength of Zn-CPS bioceramics were investigated and the related mechanism was also discussed. The results showed that ZnO could significantly enhance the sintering of CPS and improve its bending strength accordingly. The Zn-CPS bioceramic with 1 wt% ZnO sintered at 1300 degrees C exhibited a highest bending strength of 80.8 MPa. The enhanced densification of Zn-CPS bioceramics might be attributed to the liquid phase appeared during the sintering process and the formation of Ca2ZnSi2O72 (HT) nano-grains at-grain boundaries It is expected that Zn-CPS bioceramics could have both good mechanical property and excellent bioactivity. |
学科主题 | Materials Science, Ceramics |
出版者 | ELSEVIER SCI LTD |
WOS记录号 | WOS:000445993000100 |
资助机构 | This work was financially supported by National Key Research and Development Program of China (Grant No. 2017YFC1103800), National Natural Science Foundation of China (Grant No. 51672304) and International Partnership Program of Chinese Academy of Sciences (Grant No. GJHZ1760). ; This work was financially supported by National Key Research and Development Program of China (Grant No. 2017YFC1103800), National Natural Science Foundation of China (Grant No. 51672304) and International Partnership Program of Chinese Academy of Sciences (Grant No. GJHZ1760). |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/24640] |
专题 | 中国科学院上海硅酸盐研究所 |
作者单位 | 1.Chinese Acad Sci, State Key Lab High Performance Ceram & Superfine, Inst Ceram, Shanghai 200050, Peoples R China 2.Chinese Acad Sci, Anal & Testing Ctr Inorgan Mat, Inst Ceram, Shanghai 200050, Peoples R China 3.Univ Chinese Acad Sci, 19A Yuquan Rd, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Deng, Fanyan,Wang, Feng,Liu, Ziwei,et al. Enhanced mechanical property of Ca-5(PO4)(2)SiO4 bioceramic by a biocompatible sintering aid of zinc oxide[J]. CERAMICS INTERNATIONAL,2018,44(15):18352, 18362. |
APA | Deng, Fanyan,Wang, Feng,Liu, Ziwei,Kou, Huamin,Cheng, Guofeng,&Ning, Congqin.(2018).Enhanced mechanical property of Ca-5(PO4)(2)SiO4 bioceramic by a biocompatible sintering aid of zinc oxide.CERAMICS INTERNATIONAL,44(15),18352. |
MLA | Deng, Fanyan,et al."Enhanced mechanical property of Ca-5(PO4)(2)SiO4 bioceramic by a biocompatible sintering aid of zinc oxide".CERAMICS INTERNATIONAL 44.15(2018):18352. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论