Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use

CORC > 宁波材料技术与工程研究所 > 中国科学院宁波材料技术与工程研究所 > 2018专题

	Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use
	Liu, Zhixiong; Han, Jin; Xue, Qingquan; Zheng, Yaochen; Chen, Cheng; Tian, Shu; Shen, Jieze; Zhong, Mingqiang
刊名	POLYMER
	2018
卷号	154 页码:43107
关键词	Sol-gel Coatings Copper Corrosion Surface Modification Click Reaction Protection Chemistry Metals Inhibitors Delivery
英文摘要	A catalyst-free and thermal-induced S -> O acetyl migration (SOAM) reaction was occasionally found and used to fabricate the polythiol corrosion inhibitor. The route to prepare the polythiols was free of catalyst and side products. Only intramolecular migration process existed, while intermolecular migration was not found. Temperature-dependent H-1 NMR experiment showed the conversion rate of the SOAM reaction was 83% at 160 degrees C. Further heating at higher temperature or for longer reaction time, the conversion rate did not increase. It was speculated that there was equilibrium between two reversible migrations. The prepared polythiol inhibitor contains a large amount of latent thiol groups after the SOAM reaction process. The strong Cu-S bonds immediately formed and made the polythiol chains firmly anchored on the copper surface when the copper metal was coated with the polythiols. Also S-S bond formation reaction leads to dense crosslinking and film formation. Raman spectrum and SEM were used to characterized the protective film. A smooth and defect-free film with thickness of 1.9 mu m was achieved when the copper sample was immersed in the polythiol solution for 60 min. The corrosion performance of the film is obtained by potential and impedance measurements and Tafel curves by immersing in a 3.5 wt% NaCl solution. All of the coated samples exhibited significantly lower corrosion rates than the bare copper sample, and the corrosion rate decreased as the immersion time increased. The inhibtion efficiency of the polythiol inhibitor was up to 99.3%. Neutral salt spray experiments indicated that the polythiol films provided excellent protection for over one week. The polythiols were also very stable in storage and have application in designing various polyacrylate polythiols resins.
学科主题	Physics
语种	英语
公开日期	2018-12-04
内容类型	期刊论文
源URL	[http://ir.nimte.ac.cn/handle/174433/17131]
专题	2018专题
推荐引用方式 GB/T 7714	Liu, Zhixiong,Han, Jin,Xue, Qingquan,et al. Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use[J]. POLYMER,2018,154:43107.
APA	Liu, Zhixiong.,Han, Jin.,Xue, Qingquan.,Zheng, Yaochen.,Chen, Cheng.,...&Zhong, Mingqiang.(2018).Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use.POLYMER,154,43107.
MLA	Liu, Zhixiong,et al."Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use".POLYMER 154(2018):43107.