The mechanism of stress corrosion cracking of Alloy 690TT in a caustic solution containing lead | |
Hou Qiang; Liu Zhiyong; Li Chengtao; Li Xiaogang | |
刊名 | CORROSION SCIENCE |
2017 | |
卷号 | 128页码:154-163 |
ISSN号 | 0010-938X |
英文摘要 | This study investigated the PbSCC of Alloy 690TT exposed to a caustic solution at 320 degrees C. Characterization of the resulting films indicates that lead is involved in the formation of oxides and evenly distributed in the films. TEM analysis was carried out to elucidate the role of lead in IGSCC by investigating the oxides at the crack tip. Lead penetrates into the crack tip and disperses in the intergranular oxides, enhancing the oxidation of grain boundaries. Thus, microcracks initiate within oxides under stress and connect with the main SCC crack stemming from the pit, resulting in propagation of the IGSCC. |
公开日期 | 2017-12-25 |
内容类型 | 期刊论文 |
源URL | [http://ir.nimte.ac.cn/handle/174433/13547] |
专题 | 2017专题 |
推荐引用方式 GB/T 7714 | Hou Qiang,Liu Zhiyong,Li Chengtao,et al. The mechanism of stress corrosion cracking of Alloy 690TT in a caustic solution containing lead[J]. CORROSION SCIENCE,2017,128:154-163. |
APA | Hou Qiang,Liu Zhiyong,Li Chengtao,&Li Xiaogang.(2017).The mechanism of stress corrosion cracking of Alloy 690TT in a caustic solution containing lead.CORROSION SCIENCE,128,154-163. |
MLA | Hou Qiang,et al."The mechanism of stress corrosion cracking of Alloy 690TT in a caustic solution containing lead".CORROSION SCIENCE 128(2017):154-163. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论