Surface morphology and microstructure evolution of IG-110 graphite after xenon ion irradiation and subsequent annealing | |
Huang, Q; Li, JJ; Liu, RD; Yan, L; Huang, HF | |
刊名 | JOURNAL OF NUCLEAR MATERIALS |
2017 | |
卷号 | 491期号:-页码:213-220 |
关键词 | Transmission Electron-microscopy Isotropic Nuclear Graphite Fine Grain Graphite Neutron-irradiation Dimensional Changes Polycrystalline Graphite Proton Irradiation Implanted Graphite Radiation-damage Grade Graphite |
ISSN号 | 0022-3115 |
DOI | 10.1016/j.jnucmat.2017.05.013 |
文献子类 | 期刊论文 |
英文摘要 | IG-110 graphite samples were polished and irradiated with Xe ions at various fluences, then annealed at high temperatures up to 1100 degrees C. After irradiation, small hills were found on the polished surfaces, indicating an anisotropic swelling induced by irradiation. Around 30% swelling at a fluence of 2 x 10(15) ions/cm(2) was characterized using atomic force microscopy. Severe swelling of the graphite crystallites caused stresses between adjacent crystallites, but leaved no intergranular cracks on the polished surface, which was ascribed to irradiation-induced creep of graphite. The pore morphology was affected by the anisotropic swelling. We found many contracted pores but only one expanded pore, indicating a decreased porosity induced by irradiation. After annealing at 1100 degrees C, TEM characterization showed clearly increased lattice order and decreased width of the (002) diffraction arc, indicating the annihilation of dislocations and recovery of basal plane rotations. Annealing-induced recrystallization of damaged graphite led to recovery of the crystallites' swelling and many small cracks appearing on the samples' surfaces. (C) 2017 Elsevier B.V. All rights reserved. |
WOS关键词 | TRANSMISSION ELECTRON-MICROSCOPY ; ISOTROPIC NUCLEAR GRAPHITE ; FINE GRAIN GRAPHITE ; NEUTRON-IRRADIATION ; DIMENSIONAL CHANGES ; POLYCRYSTALLINE GRAPHITE ; PROTON IRRADIATION ; IMPLANTED GRAPHITE ; RADIATION-DAMAGE ; GRADE GRAPHITE |
语种 | 英语 |
WOS记录号 | WOS:000404306700024 |
内容类型 | 期刊论文 |
源URL | [http://ir.sinap.ac.cn/handle/331007/28840] |
专题 | 上海应用物理研究所_中科院上海应用物理研究所2011-2017年 |
推荐引用方式 GB/T 7714 | Huang, Q,Li, JJ,Liu, RD,et al. Surface morphology and microstructure evolution of IG-110 graphite after xenon ion irradiation and subsequent annealing[J]. JOURNAL OF NUCLEAR MATERIALS,2017,491(-):213-220. |
APA | Huang, Q,Li, JJ,Liu, RD,Yan, L,&Huang, HF.(2017).Surface morphology and microstructure evolution of IG-110 graphite after xenon ion irradiation and subsequent annealing.JOURNAL OF NUCLEAR MATERIALS,491(-),213-220. |
MLA | Huang, Q,et al."Surface morphology and microstructure evolution of IG-110 graphite after xenon ion irradiation and subsequent annealing".JOURNAL OF NUCLEAR MATERIALS 491.-(2017):213-220. |