Three-Dimensional Printing of Shape Memory Composites with Epoxy-Acrylate Hybrid Photopolymer | |
Yu, Ran1; Yang, Xin1; Zhang, Ying1; Zhao, Xiaojuan1; Wu, Xiao1,2; Zhao, Tingting1,2; Zhao, Yulei1; Huang, Wei1 | |
刊名 | ACS APPLIED MATERIALS & INTERFACES |
2017-01-18 | |
卷号 | 9期号:2页码:1820-1829 |
关键词 | 3d Printing Stereolithography Shape Memory Polymer Epoxy Acrylate |
英文摘要 | Four-dimensional printing, a new process to fabricate active materials through three-dimensional (3D) printing developed by MITs Self-Assembly Lab in 2014, has attracted more and more research and development interests recently. In this paper, a type of epoxy-acrylate hybrid photopolymer was synthesized and applied to fabricate shape memory polymers through a stereolithography 3D printing technique. The glass-to-rubbery modulus ratio of the printed sample determined by dynamic mechanical analysis is as high as 600, indicating that it may possess good shape memory properties. Fold-deploy and shape memory cycle tests were applied to evaluate its shape memory performance. The shape fixity ratio and the shape recovery ratio in ten cycles of fold-deploy tests are about 99 and 100%, respectively. The shape recovery process takes less than 20 s, indicating its rapid shape recovery rate. The shape fixity ratio and shape recovery ratio during 18 consecutive shape memory cycles are 97.44 +/- 0.08 and 100.02 +/- 0.05%, respectively, showing that the printed sample has high shape fixity ratio, shape recovery ratio, and excellent cycling stability. A tensile test at 62 degrees C demonstrates that the printed samples combine a relatively large break strain of 38% with a large recovery stress of 4.7 MPa. Besides, mechanical and thermal stability tests prove that the printed sample has good thermal stability and mechanical properties, including high strength and good toughness. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.iccas.ac.cn/handle/121111/37954] |
专题 | 化学研究所_高技术材料实验室 |
作者单位 | 1.Chinese Acad Sci, Inst Chem, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Yu, Ran,Yang, Xin,Zhang, Ying,et al. Three-Dimensional Printing of Shape Memory Composites with Epoxy-Acrylate Hybrid Photopolymer[J]. ACS APPLIED MATERIALS & INTERFACES,2017,9(2):1820-1829. |
APA | Yu, Ran.,Yang, Xin.,Zhang, Ying.,Zhao, Xiaojuan.,Wu, Xiao.,...&Huang, Wei.(2017).Three-Dimensional Printing of Shape Memory Composites with Epoxy-Acrylate Hybrid Photopolymer.ACS APPLIED MATERIALS & INTERFACES,9(2),1820-1829. |
MLA | Yu, Ran,et al."Three-Dimensional Printing of Shape Memory Composites with Epoxy-Acrylate Hybrid Photopolymer".ACS APPLIED MATERIALS & INTERFACES 9.2(2017):1820-1829. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论