Experimental study on cracking behaviour of moulded gypsum containing two non-parallel overlapping flaws under uniaxial compression | |
Afolagboye, Lekan Olatayo1,2; He, Jianming1; Wang, Sijing1 | |
刊名 | ACTA MECHANICA SINICA |
2017-04-01 | |
卷号 | 33期号:2页码:394-405 |
关键词 | Crack Coalescence Moulded Gypsum Non-parallel Flaws Primary Cracks Uniaxial Compression Test |
ISSN号 | 0567-7718 |
DOI | 10.1007/s10409-016-0624-9 |
文献子类 | Article |
英文摘要 | Failure of rock mass that is subjected to compressive loads occurs from initiation, propagation, and linkage of new cracks from preexisting fissures. Our research investigates the cracking behaviour and coalescence process in a brittle material with two non-parallel overlapping flaws using a high-speed camera. The coalescence tensile crack and tensile wing cracks were the first cracks to occur from the preexisting flaws. The initiation stresses of the primary cracks at the two tips of each flaw were simultaneous and decreased with reduced flaw inclination angle. The following types of coalescence cracks were identified between the flaws: primary tensile coalescence crack, tensile crack linkage, shear crack linkage, mixed tensile-shear crack, and indirect crack coalescence. Coalescence through tensile linkage occurred mostly at pre-peak stress. In contrast, coalescence through shear or mixed tensile-shear cracks occurred at higher stress. Overall, this study indicates that the geometry of preexisting flaws affect crack initiation and coalescence behaviour. |
WOS关键词 | ROCK-LIKE MATERIAL ; FRACTURE COALESCENCE BEHAVIOR ; UNPARALLEL FISSURES ; MECHANICAL-BEHAVIOR ; RED SANDSTONE ; PROPAGATION ; SPECIMENS ; STRENGTH ; GRANITE ; DAMAGE |
WOS研究方向 | Engineering ; Mechanics |
语种 | 英语 |
出版者 | SPRINGER HEIDELBERG |
WOS记录号 | WOS:000400856200017 |
资助机构 | National Natural Science Foundation of China(41572310 ; Strategic Priority Research Program of the Chinese Academy of Sciences(XDB10030301 ; CAS-TWAS Presidential Fellowship, University of Chinese Academy of Sciences, Beijing, China ; 41272351) ; XDB10030304) ; National Natural Science Foundation of China(41572310 ; Strategic Priority Research Program of the Chinese Academy of Sciences(XDB10030301 ; CAS-TWAS Presidential Fellowship, University of Chinese Academy of Sciences, Beijing, China ; 41272351) ; XDB10030304) ; National Natural Science Foundation of China(41572310 ; Strategic Priority Research Program of the Chinese Academy of Sciences(XDB10030301 ; CAS-TWAS Presidential Fellowship, University of Chinese Academy of Sciences, Beijing, China ; 41272351) ; XDB10030304) ; National Natural Science Foundation of China(41572310 ; Strategic Priority Research Program of the Chinese Academy of Sciences(XDB10030301 ; CAS-TWAS Presidential Fellowship, University of Chinese Academy of Sciences, Beijing, China ; 41272351) ; XDB10030304) |
内容类型 | 期刊论文 |
源URL | [http://ir.iggcas.ac.cn/handle/132A11/52952] |
专题 | 地质与地球物理研究所_中国科学院页岩气与地质工程重点实验室 |
通讯作者 | Afolagboye, Lekan Olatayo |
作者单位 | 1.Chinese Acad Sci, Inst Geol & Geophys, Key Lab Shale Gas & Geoengn, Beijing 100029, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Afolagboye, Lekan Olatayo,He, Jianming,Wang, Sijing. Experimental study on cracking behaviour of moulded gypsum containing two non-parallel overlapping flaws under uniaxial compression[J]. ACTA MECHANICA SINICA,2017,33(2):394-405. |
APA | Afolagboye, Lekan Olatayo,He, Jianming,&Wang, Sijing.(2017).Experimental study on cracking behaviour of moulded gypsum containing two non-parallel overlapping flaws under uniaxial compression.ACTA MECHANICA SINICA,33(2),394-405. |
MLA | Afolagboye, Lekan Olatayo,et al."Experimental study on cracking behaviour of moulded gypsum containing two non-parallel overlapping flaws under uniaxial compression".ACTA MECHANICA SINICA 33.2(2017):394-405. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论