Fabrication, patterning, and optical properties of nanocrystalline YVO4 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via sol-gel soft lithography | |
Yu M ; Lin J ; Wang Z ; Fu J ; Wang S ; Zhang HJ ; Han YC | |
刊名 | chemistry of materials |
2002 | |
卷号 | 14期号:5页码:2224-2231 |
关键词 | ENERGY-TRANSFER THIN-FILMS LUMINESCENCE PHOTOLUMINESCENCE GREEN |
ISSN号 | 0897-4756 |
通讯作者 | lin j |
中文摘要 | nanocrystalline yvo4:a (a = eu3+, dy3+, sm3+, er3+) phosphor films and their patterning were fabricated by a pechini sol-gel process combined with soft lithography. x-ray diffraction (xrd), fourier transform infrared spectroscopy (ft-ir), thermogravimetric and differential thermal analysis (tg-dta), atomic force microscopy (afm) and optical microscopy, uv/vis transmission and absorption spectra, photoluminescence (pl) spectra, and lifetimes were used to characterize the resulting films. the results of xrd indicated that the films began to crystallize at 400 degreesc and the crystallinity increased with the increase of annealing temperatures. transparent nonpatterned phosphor films were uniform and crack-free, which mainly consisted of grains with an average size of 90 nm. patterned gel and crystalline phosphor film bands with different widths (5-60 mum) were obtained. significant shrinkage and a few defects were observed in the patterned films during the heat treatment process. the doped rare earth ions (a) showed their characteristic emission in crystalline yvo4 phosphor films because of an efficient energy transfer from vanadate groups to them. the sm3+ and er3+ ions also showed upconversion luminescence in a yvo4 film host. both the lifetimes and pl intensity of the rare earth ions increased with increasing annealing temperature from 400 to 800 degreesc, and the optimum concentration for eu3+ was determined to be 7 mol % and those for dy3+, sm3-, and er3+ were 2 mol % of y3- in yvo4 films, respectively. |
收录类别 | SCI收录期刊论文 |
语种 | 英语 |
WOS记录号 | WOS:000175790100045 |
公开日期 | 2010-11-03 |
内容类型 | 期刊论文 |
源URL | [http://202.98.16.49/handle/322003/18593] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Yu M,Lin J,Wang Z,et al. Fabrication, patterning, and optical properties of nanocrystalline YVO4 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via sol-gel soft lithography[J]. chemistry of materials,2002,14(5):2224-2231. |
APA | Yu M.,Lin J.,Wang Z.,Fu J.,Wang S.,...&Han YC.(2002).Fabrication, patterning, and optical properties of nanocrystalline YVO4 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via sol-gel soft lithography.chemistry of materials,14(5),2224-2231. |
MLA | Yu M,et al."Fabrication, patterning, and optical properties of nanocrystalline YVO4 : A (A = Eu3+, Dy3+, Sm3+, Er3+) phosphor films via sol-gel soft lithography".chemistry of materials 14.5(2002):2224-2231. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论