Effect of Y for enhanced age hardening response and mechanical properties of Mg-Gd-Y-Zr alloys | |
Wang J ; Meng J ; Zhang DP ; Tang DX | |
刊名 | materials science and engineering a-structural materials properties microstructure and processing |
2007 | |
卷号 | 456期号:1-2页码:78-84 |
关键词 | MAGNESIUM CREEP MICROSTRUCTURE |
ISSN号 | 0921-5093 |
通讯作者 | meng j |
中文摘要 | in this study, compositional dependence of age hardening response and tensile properties were investigated for mg-10g(d-x)y-0.4zr (x = 1, 3, 5 wt.%) alloys. with increasing y content, the age hardening response of the alloys enhanced and tensile properties increased. the mg-10gd-5y-0.4zr alloy exhibited maximum tensile strength and yield strength at aged-peak hardness, and the values were 302 mpa and 289 mpa at room temperature, and 340 mpa and 267 mpa at 250 degrees c, respectively. the strong peak age hardening was attributed to the precipitation of prismatic beta' plates in a triangular arrangement. the cubic shaped beta phase was also observed at grain boundaries. the remarkable improvement in strength is associated with a uniform and high dense distribution of beta' and cubic shaped beta precipitate phases in mg matrix. elongation of mg-10gd-0.4zr alloys decreased with increasing y content, and the elongation of mg-10gd-5y-0.4zr alloy was less than 3% below 250 degrees c, whereas the alloys containing i wt.% and 3 wt.% y exhibited higher elongation than 5% at room temperature. |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000246487300012 |
公开日期 | 2010-07-13 |
内容类型 | 期刊论文 |
源URL | [http://ir.ciac.jl.cn/handle/322003/14257] |
专题 | 长春应用化学研究所_长春应用化学研究所知识产出_期刊论文 |
推荐引用方式 GB/T 7714 | Wang J,Meng J,Zhang DP,et al. Effect of Y for enhanced age hardening response and mechanical properties of Mg-Gd-Y-Zr alloys[J]. materials science and engineering a-structural materials properties microstructure and processing,2007,456(1-2):78-84. |
APA | Wang J,Meng J,Zhang DP,&Tang DX.(2007).Effect of Y for enhanced age hardening response and mechanical properties of Mg-Gd-Y-Zr alloys.materials science and engineering a-structural materials properties microstructure and processing,456(1-2),78-84. |
MLA | Wang J,et al."Effect of Y for enhanced age hardening response and mechanical properties of Mg-Gd-Y-Zr alloys".materials science and engineering a-structural materials properties microstructure and processing 456.1-2(2007):78-84. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论