Interaction of Ta and Cr on Type-I hot corrosion resistance of single crystal Ni-base superalloys | |
Chang, J. X. ; Wang, D. ; Zhang, G. ; Lou, L. H. ; Zhang, J. | |
刊名 | CORROSION SCIENCE |
2017-03-01 | |
卷号 | 117页码:35-42 |
关键词 | Molten salts Superalloys Tantalum oxide Hot corrosion |
ISSN号 | 0010-938X |
通讯作者 | Wang, D (reprint author), Chinese Acad Sci, Inst Met Res, Superalloys Div, 72 Wenhua Rd, Shenyang 110016, Peoples R China. |
中文摘要 | Type-I hot corrosion behaviour of single crystal Ni-base superalloys with different Cr and Ta contents in sodium sulphate (Na2SO4) at 900 degrees C and 950 degrees C in static air were investigated using the "deposit recoat" method. It was shown that, increasing corrosion temperature shortened the incubation period. Loss of hot corrosion resistance causing by Cr reduction cannot be compensated by increasing Ta content. The effect of Ta addition on hot corrosion resistance can be described by introducing the quantitative parameter Ta/Cr (wt.%) ratio. Interaction of Cr, Ta and temperature on hot corrosion behaviour was discussed in detail in the present paper. (C) 2017 Elsevier Ltd. All rights reserved. |
学科主题 | Materials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering |
收录类别 | SCI |
资助信息 | National Natural Science Foundation of China [51631008]; National Key Research and Development Program of China [2016YFB0701403] |
语种 | 英语 |
公开日期 | 2017-08-17 |
内容类型 | 期刊论文 |
源URL | [http://ir.imr.ac.cn/handle/321006/78269] |
专题 | 金属研究所_中国科学院金属研究所 |
推荐引用方式 GB/T 7714 | Chang, J. X.,Wang, D.,Zhang, G.,et al. Interaction of Ta and Cr on Type-I hot corrosion resistance of single crystal Ni-base superalloys[J]. CORROSION SCIENCE,2017,117:35-42. |
APA | Chang, J. X.,Wang, D.,Zhang, G.,Lou, L. H.,&Zhang, J..(2017).Interaction of Ta and Cr on Type-I hot corrosion resistance of single crystal Ni-base superalloys.CORROSION SCIENCE,117,35-42. |
MLA | Chang, J. X.,et al."Interaction of Ta and Cr on Type-I hot corrosion resistance of single crystal Ni-base superalloys".CORROSION SCIENCE 117(2017):35-42. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论