石墨烯-氧化锌复合材料及其电化学性能

CORC > 厦门大学 > 2014年第20卷

	石墨烯-氧化锌复合材料及其电化学性能; Fabrication and Electrochemical Properties of Graphene-ZnO Nanocomposite
	门传玲 ; 王婉 ; 曹军 ; MEN Chuan-ling ; WANG Wan ; CAO Jun
刊名	http://electrochem.xmu.edu.cn/CN/abstract/abstract10065.shtml
	2014-04-28
关键词	石墨烯氧化锌超级电容器纳米复合材料循环伏安测试 graphene ZnO supercapacitors nanocomposite cyclic voltammetry
英文摘要	采用Hummers法制得氧化石墨，再经溶剂热法一步合成石墨烯-氧化锌复合材料（GZO）. 在6 mol·L-1氢氧化钾电解液中，测试循环伏安曲线、交流阻抗谱图和计时电位曲线. 结果表明，石墨烯-氧化锌复合材料电极的比电容为115 F·g-1，具有较好的循环寿命，改善了超级电容器的性能.; In this work, the graphene-ZnO nanocomposite was successfully synthesized through a one-step solvothermal approach, using ethylene glycol as the solvent and reducing agent. The ZnO particles could be attached to the surfaces and edges of graphene sheet. The electrochemical performance of the nanocomposite was investigated by performing cyclic voltammetry, A.C. impedance and chronopotentiometry tests in 6 mol·L-1 KOH. The results showed that the graphene-ZnO nanocomposite exhibited a nice electrochemical specific capacitance of 115 F·g-1 determined in cyclic voltammetry test, or 71 F·g-1 evaluated in chronopotentiometry test and good reversible charge/discharge behavior.; 上海市自然科学基金项目（No. 13ZR1428200）资助; 作者联系地址：上海理工大学能源与动力工程学院上海 200093; Author's Address: University of Shanghai for Science and Technology, School of Energy and Power Engineering, Shanghai 200093, China; 通讯作者E-mail：wancxyr@gmail.com
语种	中文
出版者	厦门大学《电化学》编辑部
内容类型	期刊论文
源URL	[http://dx.doi.org/10.13208/j.electrochem.130724]
专题	2014年第20卷
推荐引用方式 GB/T 7714	门传玲,王婉,曹军,等. 石墨烯-氧化锌复合材料及其电化学性能, Fabrication and Electrochemical Properties of Graphene-ZnO Nanocomposite[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract10065.shtml,2014.
APA	门传玲,王婉,曹军,MEN Chuan-ling,WANG Wan,&CAO Jun.(2014).石墨烯-氧化锌复合材料及其电化学性能.http://electrochem.xmu.edu.cn/CN/abstract/abstract10065.shtml.
MLA	门传玲,et al."石墨烯-氧化锌复合材料及其电化学性能".http://electrochem.xmu.edu.cn/CN/abstract/abstract10065.shtml (2014).