	陶瓷表面无敏化活化法微细化学镀铜; Selective Electroless Copper Plating Micro-pattern on Ceramics Without Sensitisation and Activation
	续振林 ; 郭琦龙 ; 沈艺程 ; 赵雄超 ; 洪艳萍 ; 辜志俊 ; XU Zhen-lin
刊名	http://electrochem.xmu.edu.cn/CN/abstract/abstract8934.shtml
	2005-05-28
关键词	陶瓷基底化学镀铜活化络合剂金属化互连导线 Ceramic Electrolesscopperplating Activation Complexant Metallization Interconnection
英文摘要	本文提出一种新的化学镀铜工艺,与激光微细刻蚀技术相结合可在Al2O3基底上实现无敏化活化化学镀铜,获得光亮致密、分辨率较高(40μm),导电性良好的化学镀层.; The purpose of this article is to provide a new technology of electroless copper plating without palladium activation steps. By combining the technology of laser micro-etching with the new copper-plating bath, copper plating on ceramics was obtained. The experimental results showed that the solution used for copper electroless plating was stable and the copper coating obtained was bright,dense with good electrical conductivity.The line definition was about 40 μm. The electroless Cu films deposited from this system were gentle and required simple operating conditions.; 作者联系地址：中科院福建物质结构研究所二部,中科院福建物质结构研究所二部,中科院福建物质结构研究所二部,中科院福建物质结构研究所二部,中科院福建物质结构研究所二部,中科院福建物质结构研究所二部福建厦门361012中国科学院研究生院,北京100039 ,福建厦门361012 ,福建厦门361012中国科学院研究生院,北京100039 ,福建厦门361012 ,福建厦门361012 ,福建厦门361012; Author's Address: 1, 2, GUO Qi-long~1, SHEN Yi-cheng~1, 2, ZHAO Xiong-chao~1, HONG Yan-ping~1, GU Zhi-jun~*11.Institute of Matter Structure Chinese Academy of Sciences, Corrosion Division, Xiamen 361012,China, 2.Graduate School of the Chinese Academy of Sciences,Beijing 100039,China.
语种	中文
出版者	厦门大学《电化学》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/57917]
专题	2005年第11卷
推荐引用方式 GB/T 7714	续振林,郭琦龙,沈艺程,等. 陶瓷表面无敏化活化法微细化学镀铜, Selective Electroless Copper Plating Micro-pattern on Ceramics Without Sensitisation and Activation[J]. http://electrochem.xmu.edu.cn/CN/abstract/abstract8934.shtml,2005.
APA	续振林.,郭琦龙.,沈艺程.,赵雄超.,洪艳萍.,...&XU Zhen-lin.(2005).陶瓷表面无敏化活化法微细化学镀铜.http://electrochem.xmu.edu.cn/CN/abstract/abstract8934.shtml.
MLA	续振林,et al."陶瓷表面无敏化活化法微细化学镀铜".http://electrochem.xmu.edu.cn/CN/abstract/abstract8934.shtml (2005).