An Amorphous Carbon Nitride Composite Derived from ZIF-8 as Anode Material for Sodium-Ion Batteries
Jing-Min Fan ; Jia-Jia Chen ; Qian Zhang ; Bin-Bin Chen ; Jun Zang ; Ming-Sen Zheng ; Quan-Feng Dong
2015-06-08
关键词anodes batteries carbon nitride energy storage metal-organic frameworks
英文摘要通讯作者地址: Fan, JM; An composite comprising amorphous carbon nitride (ACN) and zinc oxide is derived from ZIF-8 by pyrolysis. The composite is a promising anode material for sodium-ion batteries. The nitrogen content of the ACN composite is as high as 20.4%, and the bonding state of nitrogen is mostly pyridinic, as determined by X-ray photoelectron spectroscopy (XPS). The composite exhibits an excellent Na+ storage performance with a reversible capacity of 430mAhg(-1) and 146mAhg(-1) at current densities of 83mAg(-1) and 8.33Ag(-1), respectively. A specific capacity of 175mAhg(-1) was maintained after 2000 cycles at 1.67Ag(-1), with only 0.016% capacity degradation per cycle. Moreover, an accelerating rate calorimetry (ARC) test demonstrates the excellent thermal stability of the composite, with a low self heating rate and high onset temperature (210 degrees C). These results shows its promise as a candidate material for high-capacity, high-rate anodes for sodium-ion batteries.; National 973 Program 2015CB251102 Key Project of NSFC U1305246 21321062
语种英语
出版者WILEY-V C H VERLAG GMBH
内容类型期刊论文
源URL[http://dspace.xmu.edu.cn/handle/2288/84984]  
专题化学化工-已发表论文
推荐引用方式
GB/T 7714
Jing-Min Fan,Jia-Jia Chen,Qian Zhang,et al. An Amorphous Carbon Nitride Composite Derived from ZIF-8 as Anode Material for Sodium-Ion Batteries[J],2015.
APA Jing-Min Fan.,Jia-Jia Chen.,Qian Zhang.,Bin-Bin Chen.,Jun Zang.,...&Quan-Feng Dong.(2015).An Amorphous Carbon Nitride Composite Derived from ZIF-8 as Anode Material for Sodium-Ion Batteries..
MLA Jing-Min Fan,et al."An Amorphous Carbon Nitride Composite Derived from ZIF-8 as Anode Material for Sodium-Ion Batteries".(2015).
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace