Electrodeposition and structure of Ni-W-B amorphous alloy | |
Huang,L ; Yang,FZ ; Xu,SK ; Zhou,SM ; Niu,ZJ ; Cao,GM ; Yang FZ(杨防祖) | |
2001-03 | |
关键词 | NICKEL-TUNGSTEN ALLOYS CHROMIUM |
英文摘要 | The electrodeposition of Ni-W-B alloy and the composition, structure and microhardness of the deposits were studied by means of electrochemical techniques. XPS, DSC and XRD. The results showed that Ni-W-B alloy electrodeposit has a lower electrochemical activity compared with Ni-W alloy. Ni-W-B allow electrodeposition was accompanied by th electroless deposition of Ni and incorporation of Na2B4O7 in the deposit. The composition of Ni-W-B alloy deposit was not remarkably affected by changes of sodium tungstate concentration and the maximum electrodeposition current efficiency was 49.9% in the electrolyte solution with [W]/[W]+[Ni] mole ratio at 0.65. The Ni-W allow obtained was present in a nanocrystalline structure, Ni-W-B was amorphous. Treatment at 400 degreesC for 2 hours caused coarsening of grain size, phase evolution for the Ni-W-B alloy and increase of microhardnesses. |
语种 | 英语 |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/62424] ![]() |
专题 | 化学化工-已发表论文 |
推荐引用方式 GB/T 7714 | Huang,L,Yang,FZ,Xu,SK,et al. Electrodeposition and structure of Ni-W-B amorphous alloy[J],2001. |
APA | Huang,L.,Yang,FZ.,Xu,SK.,Zhou,SM.,Niu,ZJ.,...&杨防祖.(2001).Electrodeposition and structure of Ni-W-B amorphous alloy.. |
MLA | Huang,L,et al."Electrodeposition and structure of Ni-W-B amorphous alloy".(2001). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论