	热处理对高硫化氢合成气一步法制甲硫醇K_2MoO_4-NiO/SiO_2催化剂结构及性能的影响; Effect of Thermal Treatment on Structure and Catalytic Performance of K_2MoO_4-NiO/SiO_2 Catalyst for One-Step Synthesis of Methanethiol from High H_2S-Containing Syngas
	王琪(合肥工业大学化学工程学院) ; 郝影娟 ; 陈爱平 ; 杨意泉
	2010-02
关键词	钼镍基催化剂 焙烧 一步合成法 硫化氢 合成气 甲硫醇 molybdenum-nickel-based catalyst calcination one-step synthesis hydrogen sulfide syngas methanethiol
英文摘要	王 琪. Tel: (0551)2901458; Fax: (0551)2901450; E-mail: qiwanghfut@126.com; [中文文摘]在不同焙烧温度和焙烧气氛下对共浸渍法制备的K2MoO4-NiO/SiO2催化剂进行热处理,并采用X射线衍射、热重-差示扫描量热、氢气程序升温还原、拉曼光谱和电子自旋共振波谱等手段对催化剂进行了表征,同时考察了催化剂催化高硫化氢合成气一步法制甲硫醇的性能.结果表明,由于催化剂中所含柠檬酸氧化放热,空气中焙烧的催化剂发生严重烧结.随着焙烧温度的升高,八面体配位的Mo(Oh)逐渐向四面体配位的Mo(Td)转变,导致催化剂的还原能力降低,配位不饱和Mo(CO吸附位)减少,因而CO转化率降低.甲硫醇的生成与Mo–S–K相密切相关,而MoS2晶相表面主要生成烃类.与氮气中焙烧的催化剂相比,空气中焙烧的催化剂表面的MoS2相较多,而Mo–S–K相较少,因此具有更高的烃类选择性和更低的甲硫醇选择性.[英文摘要]K2MoO4-NiO/SiO2 catalyst samples prepared by the co-impregnation method were calcined at different temperatures and atmosphere. X-ray diffraction, thermal gravimetric-differential scanning calorimetry, hydrogen temperature-programmed reduction, Raman spectroscopy, and electron spin resonance techniques were used to characterize the catalyst samples. The catalytic performance of the catalyst for one-step synthesis of methanethiol from high H2S-containing syngas was evaluated. The results showed that the catalyst calcined in air sintered seriously because of the heat release from citric acid oxidation. With the increase of calcination temperature, octahedral coordination Mo(Oh) gradually changed into tetrahedral coordination Mo(Td), which made the reduction of Mo6+ more difficult, decreased the number of CO adsorption sites (coordinatively unsaturated sites) of Mo, and at last led to the decrease of CO conversion. Methanethiol synthesis was closely related to the Mo–S–K phase, and hydrocarbon synthesis was related to the MoS2 phase. Compared with the catalyst calcined in N2, there were more MoS2 phase and less Mo–S–K phase on the surface of the catalyst calcined in air, resulting in the higher selectivity for hydrocarbon and lower selectivity for CH3SH.
语种	中文
出版者	《催化学报》编辑部
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/3756]
专题	化学化工－已发表论文
推荐引用方式 GB/T 7714	王琪(合肥工业大学化学工程学院),郝影娟,陈爱平,等. 热处理对高硫化氢合成气一步法制甲硫醇K_2MoO_4-NiO/SiO_2催化剂结构及性能的影响, Effect of Thermal Treatment on Structure and Catalytic Performance of K_2MoO_4-NiO/SiO_2 Catalyst for One-Step Synthesis of Methanethiol from High H_2S-Containing Syngas[J],2010.
APA	王琪,郝影娟,陈爱平,&杨意泉.(2010).热处理对高硫化氢合成气一步法制甲硫醇K_2MoO_4-NiO/SiO_2催化剂结构及性能的影响..
MLA	王琪,et al."热处理对高硫化氢合成气一步法制甲硫醇K_2MoO_4-NiO/SiO_2催化剂结构及性能的影响".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。