	PbO系玻璃的改进及Bi_2O_3系封接玻璃的研制; The Studies on Improvement of PbO System Glass and Preparation of Bi_2O_3 System Sealing Glass
	刘洪学 ; 张计华 ; 曾人杰
	2006-11
关键词	封接玻璃 无铅玻璃 微晶玻璃 热膨胀系数 sealing glass lead-free glass glass ceramics thermal expansion coefficient
英文摘要	[中文文摘]以氧化铅或氧化铋、氧化钙、硼酸、硫酸锌、二氧化硅和氧化镁为原料,通过高温熔融和微晶化,成功地制备出具有低熔点高膨胀系数的PbO系统微晶封接玻璃和Bi2O3系统微晶封接玻璃.分别用X射线衍射分析(XRD)、光学显微镜、热膨胀系数分析(DIL)和差热曲线分析(DTA)等方法对样品或原料混合物进行表征,分别讨论了PbO系统和Bi2O3系统微晶封接玻璃在制备工艺过程中对样品性能产生影响的主要因素.结果表明:Bi2O3系统和PbO系统都能形成玻璃;都可微晶化;PbO系微晶封接玻璃的熔化温度为365℃,最佳微晶化温度和时间分别为350~400℃和2 h,膨胀系数为12.68×10-6/℃;Bi2O3系微晶封接玻璃的熔化温度为460℃,最佳微晶化温度和时间分别为440~500℃和2 h,膨胀系数为12.06×10-6/℃.[英文文摘]The PbO system and the Bi_2O_3 system sealing glass ceramics with low melting temperature and high expansion coefficient were successfully prepared by sintering and crystallization and using PbO or Bi_2O_3,CaO,H_3BO_3,SiO_2,MgO and ZnSO_4·7H_2O as raw materials.All the samples and the mixed raw materials were characterized by employing XRD,optical microscope,DIL and DTA techniques.The main factors affecting the properties of all the samples of both flint sealing glass ceramics and Bi_2O_3 system lead-free sealing glass ceramics were discussed. It is indicated that both systems can form glass states and glass ceramics states ;and the melting temperature of flint sealing glass ceramics is 365 ℃,the optimal micro2crystallizing temperature and times are 350～400 ℃ and 2 h ,the thermal expansion coefficient is 12. 68 ×10 - 6 / ℃;the melting temperature of lead2f ree sealing glass ceramics is 460 ℃,the optimal micro2crystallizing temperatures and times are 440～500 ℃and 2 h ,the thermal expansion coefficient is 12. 06 ×10 - 6 / ℃.
语种	中文
出版者	厦门大学
内容类型	期刊论文
源URL	[http://dspace.xmu.edu.cn/handle/2288/3076]
专题	化学化工－已发表论文
推荐引用方式 GB/T 7714	刘洪学,张计华,曾人杰. PbO系玻璃的改进及Bi_2O_3系封接玻璃的研制, The Studies on Improvement of PbO System Glass and Preparation of Bi_2O_3 System Sealing Glass[J],2006.
APA	刘洪学,张计华,&曾人杰.(2006).PbO系玻璃的改进及Bi_2O_3系封接玻璃的研制..
MLA	刘洪学,et al."PbO系玻璃的改进及Bi_2O_3系封接玻璃的研制".(2006).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。