氧含量对Co-SiC纤维结构与性能的影响; The influence of oxygen content on the structure and properties of Co-SiC fibers | |
刘玲 ; 陈剑铭 ; 丁绍楠 ; 李风萍 ; 姚艳波 ; 刘安华 | |
2014-12-30 | |
关键词 | 聚碳硅烷 氧含量 含钴SiC纤维 电磁性能 polycarbosilane oxygen content cobalt-containing silicon carbide fibers electromagnetic property |
英文摘要 | 系统研究了含钴聚碳硅烷交联丝的氧含量对所成含钴碳化硅(CO-SIC)纤维结构与性能的影响。研究结果显示,较之交联丝CO-PCS-AIr,CO-PCS-O2的氧含量较高,陶瓷产率较高,所成纤维的SICXOy相含量较高、β-SIC和COSI晶粒的增长速度较快,晶粒的尺寸较大,达到最大力学性能的烧结温度较低,电阻率也较低。该纤维电阻率在100~103Ω·CM之间可调,且具有一定的磁性,有望用作吸波纤维。; In this work,it was systematically studied that how oxygen content of cured cobalt-containing polycarbosilance(PCS) fibers influences the structure and properties of cobalt-containing silicon carbide(Co-Si C) fibers.Compared to cured Co-PCS-air fibers,Co-PCS-O2 fibers have a higher oxygen content and higher ceramic yield.For Co-PCS-O2 fibers derived from cured Co-PCS-O2,lower pyrolysis temperature was required to reach maximum mechanical properties.And higher Si CxOycontent,higher growing speed and final sizes of β-Si C and Co Si grains and lower electrical conductivity were observed.Co-PCS-O2 fibers have a electrical conductivity controllable between 100-103Ω·cm and were magnetic to some degree,enabling this kind of fibers to have the potential to be used as wave-absorbing materials.; 国家自然科学基金面上资助项目(51002127;51072169) |
语种 | zh_CN |
内容类型 | 期刊论文 |
源URL | [http://dspace.xmu.edu.cn/handle/2288/98484] |
专题 | 材料学院-已发表论文 |
推荐引用方式 GB/T 7714 | 刘玲,陈剑铭,丁绍楠,等. 氧含量对Co-SiC纤维结构与性能的影响, The influence of oxygen content on the structure and properties of Co-SiC fibers[J],2014. |
APA | 刘玲,陈剑铭,丁绍楠,李风萍,姚艳波,&刘安华.(2014).氧含量对Co-SiC纤维结构与性能的影响.. |
MLA | 刘玲,et al."氧含量对Co-SiC纤维结构与性能的影响".(2014). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论