A calcium ion-imprinted porous film prepared from a cellulose-alginate composite
Wang, Yong ; Zhu, Shiqin ; Liao, Yunying ; Xiong, Xiaopeng ; Xiong XP(熊晓鹏)
刊名http://dx.doi.org/10.1007/s10965-014-0612-3
2014
关键词Alginate Calcium Cellulose Composite films Ions Mechanical properties Sodium alginate Solutions
英文摘要An ion-imprinted (IIP) film has been successfully prepared in this work. Firstly, mixture solution of cellulose and alginate was obtained by dissolving those polymers in a NaOH/urea aqueous solution. Then the mixture solution was cast onto glass plate and coagulated in CaCl2 aqueous solution bath to prepare a composite film. The matrix of the film was further fixed by cross-linking. Finally, the chelated Ca2+ in the matrix was removed to obtain the IIP film. The IIP film was characterized to show satisfactory mechanical properties, and to exhibit porous mesh network microstructure. The equilibrium swelling ratio of the IIP film was determined to be 700?%. The IIP film was immersed into Ca2+, Ca2+/Cu2+, Ca2+/Zn2+ and Ca2+/Mg2+ solutions to check the adsorption behavior, respectively. The results indicate that the IIP film displayed highly selective Ca2+ recognition, and the presence of additional cations had little effect on the Ca2+ recognition. Thus prepared Ca2+ imprinted film have potential applications in fields such as hard water softening, and Ca2+ enrichment or recognition.
语种英语
出版者Kluwer Academic Publishers
内容类型期刊论文
源URL[http://dspace.xmu.edu.cn/handle/2288/87416]  
专题材料学院-已发表论文
推荐引用方式
GB/T 7714
Wang, Yong,Zhu, Shiqin,Liao, Yunying,et al. A calcium ion-imprinted porous film prepared from a cellulose-alginate composite[J]. http://dx.doi.org/10.1007/s10965-014-0612-3,2014.
APA Wang, Yong,Zhu, Shiqin,Liao, Yunying,Xiong, Xiaopeng,&熊晓鹏.(2014).A calcium ion-imprinted porous film prepared from a cellulose-alginate composite.http://dx.doi.org/10.1007/s10965-014-0612-3.
MLA Wang, Yong,et al."A calcium ion-imprinted porous film prepared from a cellulose-alginate composite".http://dx.doi.org/10.1007/s10965-014-0612-3 (2014).
个性服务
查看访问统计
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。


©版权所有 ©2017 CSpace - Powered by CSpace