Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes | |
Yi-ming Jiang ; Bo-tian Li ; Wei-jia Wang ; Min Xu ; Kan CY(阚成友) ; Yi-ming Jiang ; Bo-tian Li ; Wei-jia Wang ; Min Xu ; Cheng-you Kan | |
2016-03-30 ; 2016-03-30 | |
关键词 | Emulsion polymerization Hollow morphology Crosslinking agent Core/shell mass ratio O645 |
其他题名 | Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes |
中文摘要 | Three-layer core/shell latex particles with various shell crosslinking level and shell thickness were prepared by multistep emulsion polymerization, and the hollow latex particles with different morphologies were then obtained after alkali post-treatment. Influences of divinyl benzene(DVB) content and the core/shell mass ratio on emulsion polymerization and particle morphology were investigated. Results showed that with the increase of DVB content, the percentage of total amount of ―COOH on the particle surface and free in aqueous phase(PSFa) decreased, and the morphology of the post-treated particles underwent evolution from cracked, intact hollow to deficient swelling structure. Decreasing the core/shell mass ratio could not only make more carboxyl groups encapsulated by the shell, but also increase the shell resistance to the swelling of the core. The uniform hollow latex particles with intact morphology were obtained when the DVB content was 3.54 wt% and the core/shell mass ratio was 1/6.; Three-layer core/shell latex particles with various shell crosslinking level and shell thickness were prepared by multistep emulsion polymerization, and the hollow latex particles with different morphologies were then obtained after alkali post-treatment. Influences of divinyl benzene(DVB) content and the core/shell mass ratio on emulsion polymerization and particle morphology were investigated. Results showed that with the increase of DVB content, the percentage of total amount of ―COOH on the particle surface and free in aqueous phase(PSFa) decreased, and the morphology of the post-treated particles underwent evolution from cracked, intact hollow to deficient swelling structure. Decreasing the core/shell mass ratio could not only make more carboxyl groups encapsulated by the shell, but also increase the shell resistance to the swelling of the core. The uniform hollow latex particles with intact morphology were obtained when the DVB content was 3.54 wt% and the core/shell mass ratio was 1/6. |
语种 | 英语 ; 英语 |
内容类型 | 期刊论文 |
源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/144103] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | Yi-ming Jiang,Bo-tian Li,Wei-jia Wang,et al. Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes[J],2016, 2016. |
APA | Yi-ming Jiang.,Bo-tian Li.,Wei-jia Wang.,Min Xu.,阚成友.,...&Cheng-you Kan.(2016).Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes.. |
MLA | Yi-ming Jiang,et al."Effect of the Shell Crosslinking Level and Core/Shell Ratio on the Morphology of Latex Particles in the Preparation of Hollow Latexes".(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论