	200 keV Xe离子辐照后国产T92钢微结构变化研究
	冯伟 ; 黄晨 ; 杜爱兵 ; 李正操 ; FENG Wei ; HUANG Chen ; DU Ai-bing ; LI Zheng-cao
	2016-03-30 ; 2016-03-30
关键词	T92钢 离子辐照 铁素体/马氏体钢 外套管材料 TL341
其他题名	Microstructure Changes of Domestic T92 Steel Irradiated by 200 keV Xe Ions
中文摘要	对国产T92钢进行200keV的Xe离子辐照试验,使用透射电子显微镜(TEM)考察该能量下不同辐照损伤剂量对其微观结构的影响,研究结果表明:T92钢典型的微观组织结构主要包括马氏体板条结构,碳、氮化合物颗粒和位错网络;辐照导致M23C6颗粒出现非晶化,且随着辐照损伤剂量的增加,非晶化越来越明显;辐照损伤剂量较小(1.4dpa和6.8dpa)时,辐照试样中出现黑斑结构(空位和间隙原子簇),所有的辐照试样中没有发现辐照产生的位错环和空洞。; Domestic T92 steel was irradiated by 200 keV Xe ions.The effects of irradiation damage dose on microstructure of T92 steel were investigated with ransmission lectron icroscope(TEM).The results showed that the typical microstructure of T92 steel included martensite lath structure,carbides,nitrides and dislocation network;M23C6particles in the irradiated samples appeared amorphous,became evident with increasing the irradiation damage dose;Black spots(vacancy and interstitial clusters)were found in samples which were irradiated at lower doses(14.dpa and 6.8dpa),and no dislocation loops and cavities were found in all irradiated samples.
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/142231]
专题	清华大学
推荐引用方式 GB/T 7714	冯伟,黄晨,杜爱兵,等. 200 keV Xe离子辐照后国产T92钢微结构变化研究[J],2016, 2016.
APA	冯伟.,黄晨.,杜爱兵.,李正操.,FENG Wei.,...&LI Zheng-cao.(2016).200 keV Xe离子辐照后国产T92钢微结构变化研究..
MLA	冯伟,et al."200 keV Xe离子辐照后国产T92钢微结构变化研究".(2016).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。