Li-,Sb-和Ta-共掺杂(K,Na)NbO_3陶瓷的低温烧结 | |
张辉 ; 王晓慧 ; 方建 ; 沈正波 ; 郝亚楠 ; ZHANG Hui ; WANG Xiao-hui ; FANG Jian ; SHEN Zheng-bo ; HAO Ya-nan | |
2016-03-30 ; 2016-03-30 | |
关键词 | 压电陶瓷 低温烧结 (K,Na)NbO3 Piezoelectric ceramic Low temperature sintering (K Na)NbO3 TQ174.652.4 |
其他题名 | Low Temperature Sintering of Li-,Sb-and Ta-Modified(K,Na)NbO_3 Ceramic |
中文摘要 | 采用水基溶胶-凝胶法合成的Li-,Sb-和Ta-共掺杂的(K,Na)NbO3(LTS-KNN)纳米粉体,在1000℃低温烧结2h,成功制备出高性能的(Na0.52K0.44Li0.04)(Nb0.86Ta0.06Sb0.08)O3无铅压电陶瓷,它的d33,kp,k,tanδ,Pr,Ec及相对密度分别达到311pC/N,46.8%,1545,0.024,15.1μC/cm2,1.21kV/mm及98.6%。; Li-,Sb-and Ta-modified(K,Na)NbO3(LTS-KNN)nano-powder was prepared using a water-based sol-gel method.High performance(Na0.52K0.44Li0.04)(Nb0.86Ta0.06Sb0.08)O3ceramic was successfully prepared at a low sintering temperature of 1000℃for 2hby use of the nanopowder,and its d33,kp, k,tanδ,Pr,Ecand relative density are 311pC/N,46.8%,1545,0.024,15.1μC/cm2,1.21kV/mm and 98.6%respectively. |
语种 | 中文 ; 中文 |
内容类型 | 期刊论文 |
源URL | [http://ir.lib.tsinghua.edu.cn/ir/item.do?handle=123456789/141666] |
专题 | 清华大学 |
推荐引用方式 GB/T 7714 | 张辉,王晓慧,方建,等. Li-,Sb-和Ta-共掺杂(K,Na)NbO_3陶瓷的低温烧结[J],2016, 2016. |
APA | 张辉.,王晓慧.,方建.,沈正波.,郝亚楠.,...&HAO Ya-nan.(2016).Li-,Sb-和Ta-共掺杂(K,Na)NbO_3陶瓷的低温烧结.. |
MLA | 张辉,et al."Li-,Sb-和Ta-共掺杂(K,Na)NbO_3陶瓷的低温烧结".(2016). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论