	冷拔Q235钢丝的高强脉冲电流“热”处理
	姚可夫 ; 邱胜宝 ; 张长青 ; Yao Kefu ; Qiu Shengbao ; Zhang Changqing
	2010-07-19 ; 2010-07-19
关键词	高强脉冲电流 Q235钢丝 冷拔 热处理 力学性能 high-density pulsing current Q235 steel wire cold drawn heat treatment mechanical property TG356.26
其他题名	High-density Pulsing Current Treatment of Cold-drawn Q235 Steel Wire
中文摘要	在冷拔变形后,Q235钢丝的屈服强度和抗拉强度均大幅升高,常常需要采用退火热处理方法来实现钢丝软化。采用高强脉冲电流处理冷拔Q235钢丝时,在4 s内将抗拉强度降低至700 MPa以下,在20 s内能使冷拔钢丝的力学性能基本恢复,达到650℃退火30 min的效果,是一种快速、高效的新型冷拔钢丝"热"处理方法。; The yield strength and tensile strength of Q235 steel wire raise after cold drawn,demand adopting anneal treatment to soften usually.If adopting high-density pulsing current to treat cold drawn Q235 steel wire,the tensile strength will be decreased bellow 700 MPa within 4 second,the mechanical property of cold drawn will be recovered within 20 second,it can reach the effect of 650 ℃ anneal within 30 min,this is a kind of new type 'heat treatment' method for cold drawn steel wire fast and high efficiency.; 国家自然科学基金(59475056); 北京市自然科学基金项目(39621); 清华大学骨干人才计划项目(922144)
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/76045]
专题	清华大学
推荐引用方式 GB/T 7714	姚可夫,邱胜宝,张长青,等. 冷拔Q235钢丝的高强脉冲电流“热”处理[J],2010, 2010.
APA	姚可夫,邱胜宝,张长青,Yao Kefu,Qiu Shengbao,&Zhang Changqing.(2010).冷拔Q235钢丝的高强脉冲电流“热”处理..
MLA	姚可夫,et al."冷拔Q235钢丝的高强脉冲电流“热”处理".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。