	银线表面浸涂法制备Bi_2Sr_2Ca_1Cu_2O_x超导膜
	宋洋 ; 赵亮 ; 李霈 ; 瞿体明 ; 韩征和 ; 黄勇 ; SONG Yang ; ZHAO Liang ; LI Pei ; QU Timing ; HAN Zhenghe ; HUANG Yong
	2010-06-10 ; 2010-06-10
关键词	浸涂 银线 局部熔化温度 固相烧结温度 后退火 临界温度 时效 dip-coating silver wire partial melting temperature solid phase sintering temperature post-annealing critical tempera- ture time effect TM26
其他题名	PREPARATION OF Bi_2Sr_2Ca_1C_u_2O_x SUPERCONDUCTING FILMS ON Ag WIRES BY DIP-COATING METHOD
中文摘要	通过浸涂法在银圆线表面制备了Bi2Sr2Ca1Cu2Ox(Bi–2212)超导厚膜。在热处理过程中,局部熔化温度和固相烧结温度对Bi–2212相的形成起关键作用。表面涂覆的直径为0.5mm银线在液氮温度、0T磁场下临界电流密度可达10000A/cm2。系统研究了在不同氧分压下,经不同温度退火处理后样品的临界温度Tc值,结果表明:最优退火温度为760℃,样品的Tc值为96.98K,氧分压越高,样品的Tc值越大。此外,Bi–2212材料在空气中放置具有时间效应,会对Tc产生影响。; Bi2Sr2Ca1Cu2Ox (Bi–2212) thick films on Ag wires were prepared by using the dip-coating method. It was found that the partial melting temperature and solid phase sintering temperature parameters during heat treatment strongly influence the phase for- mation of Bi–2212. The critical current density of dip-coated thin wire with a diameter of 0.5 mm can reach 10 000 A/cm2 at liquid nitrogen temperature and at 0 T magnetic field. Post-annealing treatments at different temperatures and oxygen partial pressures were executed in order to study the variation of critical temperature (Tc) values. Results show that the optimal post-annealing temperature is 760 ℃, and the corresponding Tc value is 96.98 K. During the post-annealing process, the higher the oxygen partial pressure is, the higher the Tc value will be. Furthermore, the properties of Bi–2212 materials have time effects when exposed to air, causing their critical temperature to change.; 教育部学科建设专项基金(985)资助项目
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/61757]
专题	清华大学
推荐引用方式 GB/T 7714	宋洋,赵亮,李霈,等. 银线表面浸涂法制备Bi_2Sr_2Ca_1Cu_2O_x超导膜[J],2010, 2010.
APA	宋洋.,赵亮.,李霈.,瞿体明.,韩征和.,...&HUANG Yong.(2010).银线表面浸涂法制备Bi_2Sr_2Ca_1Cu_2O_x超导膜..
MLA	宋洋,et al."银线表面浸涂法制备Bi_2Sr_2Ca_1Cu_2O_x超导膜".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。