	冷轧多晶纯镍中晶界对显微硬度和微观组织结构的影响
	黄天林 ; 陈宏生 ; 刘伟 ; Andrew Godfrey ; 刘庆 ; Huang Tianlin ; Chen Hongsheng ; Liu Wei ; Andrew Godfrey ; Liu Qing
	2010-06-10 ; 2010-06-10
关键词	形变 多晶纯镍 背散射电子衬度像 显微硬度 微观组织 deformation polycrystalline nickel microhardness BSE image microstructure TG335.12
其他题名	Effect of Grain Boundaries on Deformation Structure and Microhardness in Cold-Rolled Polycrystalline Nickel
中文摘要	纯度为99.9%的多晶镍(晶粒尺寸为0.5~2 mm),被轧制到55%形变量,用测试显微硬度的手段研究选定晶粒内部的形变不均匀性,用扫描电镜(SEM)上的背散射电子衬度成像分析晶粒内不同位置的微观组织的变化。结果表明,与轧制方向成较大角度的晶界的影响导致晶粒内形变的不均匀性,造成微观组织及形变储能的不同,宏观上表现为显微硬度的不同。; Pure(99.9%) polycrystalline nickel(grain size about 0.5～2 mm) was cold-rolled to reductions of 55%.In the grains on the sample,the microhardness distribution was measured,the microstructure was analysed by SEM,and orientation distribution was analysed by EBSD technology.The combination of orientation-microstructure-microhardness showed the grain the boundaries which had large angle to the RD direction had significant effect on the microstructure and microhardness near to them.; 国家自然科学基金重点项目(50231030)资助
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/61413]
专题	清华大学
推荐引用方式 GB/T 7714	黄天林,陈宏生,刘伟,等. 冷轧多晶纯镍中晶界对显微硬度和微观组织结构的影响[J],2010, 2010.
APA	黄天林.,陈宏生.,刘伟.,Andrew Godfrey.,刘庆.,...&Liu Qing.(2010).冷轧多晶纯镍中晶界对显微硬度和微观组织结构的影响..
MLA	黄天林,et al."冷轧多晶纯镍中晶界对显微硬度和微观组织结构的影响".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。