Study of Al2O3/MgF2 HR coatings at 355 nm | |
Zhan MQ(占美琼) ; Gao WD(高卫东) ; Tan TY(谭天亚) ; He HB(贺洪波) ; Shao JD(邵建达) ; Fan ZX(范正修) | |
刊名 | vacuum
![]() |
2005 | |
卷号 | 79期号:1-2页码:90 |
关键词 | vacuum annealing structure absorption LIDT |
ISSN号 | 0042-207x |
中文摘要 | with the present work we tried to study the effective methods to improve the laser-induced damage threshold (lidt) and reflectance of hr coatings at 355 nm. the work presented in this paper wits part of an ongoing study about vacuum annealing. it was dedicated to study the effects of vacuum annealing with different temperature gradients on the structure, optical properties and laser-induced damage threshold (lidt) of 355nm al2o3/mgf2hr coatings. a number of samples were prepared by electron beam evaporation using the same deposition process with an optimal deposition temperature of 280 degrees c. after deposition, samples were annealed in the coating chamber for 3 h with different temperature gradients. morphologies of the samples were observed by leica-dmrxe. microscope, structure of the samples had been characterized by x-ray diffraction (xrd). transmittance and reflectance of the samples were measured by lambda 900 spectrometer, the lidt of the samples was measured by a 355 nm nd:yag laser with a pulse width of 8 ns. it was found that the temperature gradient of vacuum annealing had significant effects on the morphology, structure, absorption, and lidt of the samples, (c) 2005 elsevier ltd. all rights reserved. |
学科主题 | 光学薄膜 |
收录类别 | EI |
语种 | 英语 |
WOS记录号 | WOS:000230261100013 |
公开日期 | 2009-09-22 |
内容类型 | 期刊论文 |
源URL | [http://ir.siom.ac.cn/handle/181231/4250] ![]() |
专题 | 上海光学精密机械研究所_光学薄膜技术研究与发展中心 |
推荐引用方式 GB/T 7714 | Zhan MQ,Gao WD,Tan TY,et al. Study of Al2O3/MgF2 HR coatings at 355 nm[J]. vacuum,2005,79(1-2):90, 93. |
APA | 占美琼,高卫东,谭天亚,贺洪波,邵建达,&范正修.(2005).Study of Al2O3/MgF2 HR coatings at 355 nm.vacuum,79(1-2),90. |
MLA | 占美琼,et al."Study of Al2O3/MgF2 HR coatings at 355 nm".vacuum 79.1-2(2005):90. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论