| 锌合金压铸射嘴身失效行为分析 | |
| 姜海荣 ; 张铁军 ; 李培杰 ; Jiang Hairong ; Zhang Tiejun ; Li Peijie | |
| 2010-06-08 ; 2010-06-08 | |
| 关键词 | 锌合金压铸 磨具钢 射嘴身 失效 Die Casting of Zinc Alloy Tool,Steel,Nozzle Body,Failure TG249.2 |
| 其他题名 | The Analysis of Influing Factor of the Failure of Nozzle Body in Zinc-alloy Die Casting |
| 中文摘要 | 针对锌合金压铸时采用M300耐蚀模具钢出现的射嘴身早期失效问题,通过组织分析发现,射嘴身材料中存在着的大量夹杂物和网状碳化物的缺陷以及M300钢本身的高温回火脆性,是射嘴身失效的主要原因。压铸时高速高压的锌合金熔体会与M300钢发生化学反应,生成Fe-Zn相的腐蚀产物,在射嘴身内腔腐蚀出沟槽,而高速锌合金熔体的冲击应力又进一步诱发沟槽内裂纹的扩展,从而促使了早期失效行为的发生。; On the base of the failure of nozzle body-made of M300 steel-in zinc-alloy die casting,through the analysising of the structure,it was found that the exsisting of much inclusion and reticular defect anditself high temper brittlenesswere is the main factor.The first factor is that the heated steel contained too much net-like distributed carbides and non-homogeneous non-metallic inclusions,which leads to low impact toughness.The second major factor for the failure is that the corrosion of M300 in zinc alloy melt can be characterized as alloying (of Fe-Zn) and dissolution (of Cr atoms into zinc alloy melt),which causes stresses-corrosion.; 烟台大学青年基金资助项目(JX06Z15) |
| 语种 | 中文 ; 中文 |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/48020]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | 姜海荣,张铁军,李培杰,等. 锌合金压铸射嘴身失效行为分析[J],2010, 2010. |
| APA | 姜海荣,张铁军,李培杰,Jiang Hairong,Zhang Tiejun,&Li Peijie.(2010).锌合金压铸射嘴身失效行为分析.. |
| MLA | 姜海荣,et al."锌合金压铸射嘴身失效行为分析".(2010). |
| 个性服务 |
| 查看访问统计 |
| 相关权益政策 |
| 暂无数据 |
| 收藏/分享 |
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论