	低温下铁路钢轨钢材及铝热焊缝拉伸试件断口分析
	胡宗文 ; 王元清 ; 石永久 ; 奚望 ; HU Zong-wen ; WANG Yuan-qing ; SHI Yong-jiu ; XI Wang
	2010-06-07 ; 2010-06-07
关键词	钢轨钢材 铝热焊缝 低温 拉伸 韧性 断口扫描 rail steel thermit welding low temperature tensile toughness fracture scanning U213.4
其他题名	STUDY ON THE FRACTURE SCANNING OF RAIL STEEL AND THERMIT WELDING AFTER THE TENSILE TEST AT LOW TEMPERATURE
中文摘要	在国内常用钢轨钢材及其铝热焊缝的低温拉伸试验结果的基础上,利用扫描电子显微镜分析各自的断口微观形貌,得出其破坏的微观机理,进而从断口形貌的角度解释钢轨钢材及其铝热焊缝的低温下抗断裂性能。研究结果表明钢材及焊缝低温下的脆性特征,其中,U71Mn要好于U75V钢材,而与钢材相比焊缝的韧性相对较差。; Basing on the results of the tensile test of rail steel and thermit welding which are popular domestically,this paper uses scanning electron microscope to analyze the fracture micro-morphology,finds the fracture microscopic mechanism,and lastly interprets the anti-fracture property at low temperature from fracture morphology viewpoint.The result shows the brittle feature of rail steel and welding at low temperature,among which U71Mn is better than U75V,and the welding is relatively worse than steel.; 国家自然科学基金项目(50778102); 铁道部-清华大学科技研究基金资助项目(t200410)
语种	中文 ; 中文
内容类型	期刊论文
源URL	[http://hdl.handle.net/123456789/47025]
专题	清华大学
推荐引用方式 GB/T 7714	胡宗文,王元清,石永久,等. 低温下铁路钢轨钢材及铝热焊缝拉伸试件断口分析[J],2010, 2010.
APA	胡宗文.,王元清.,石永久.,奚望.,HU Zong-wen.,...&XI Wang.(2010).低温下铁路钢轨钢材及铝热焊缝拉伸试件断口分析..
MLA	胡宗文,et al."低温下铁路钢轨钢材及铝热焊缝拉伸试件断口分析".(2010).

个性服务

查看访问统计

相关权益政策

暂无数据

收藏/分享

除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。