| Experimental study of micro-cracks in stress corrosion of fiber reinforced composites | |
| Dai, Jianjun ; Yao, Xuefeng ; Liang, Xidong ; Yeh, H. Y. | |
| 2010-05-06 ; 2010-05-06 | |
| 关键词 | micro-crack stress corrosion cracking glass-fiber reinforced composite fracture E-GLASS/POLYMER COMPOSITES ACOUSTIC-EMISSION ALIGNED GRP INITIATION FRACTURE GROWTH MODEL Materials Science, Characterization & Testing Polymer Science |
| 中文摘要 | Micro-cracks with a depth of 30-40 mu m are formed on the surface of glass-fiber reinforced plastics (GFRP) rod, which could lead to the stress corrosion crack propagation along the original direction and developing dominant influence on the stress corrosion cracking (SCC) performance of the composite material. Micro-cracks with different depth and angles were simulated on the surface of GFRP rod. The strain response histories around the micro-crack during the whole stress corrosion test of the GFRP rod were obtained. The effects of depth and angle of micro-crack on SCC of GFRP rod were analyzed. The stress corrosion fracture times of GFRP rod with micro-cracks of different depth and angle were obtained. (C) 2006 Elsevier Ltd. All rights reserved. |
| 语种 | 英语 ; 英语 |
| 出版者 | ELSEVIER SCI LTD ; OXFORD ; THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND |
| 内容类型 | 期刊论文 |
| 源URL | [http://hdl.handle.net/123456789/10601]  |
| 专题 | 清华大学 |
| 推荐引用方式 GB/T 7714 | Dai, Jianjun,Yao, Xuefeng,Liang, Xidong,et al. Experimental study of micro-cracks in stress corrosion of fiber reinforced composites[J],2010, 2010. |
| APA | Dai, Jianjun,Yao, Xuefeng,Liang, Xidong,&Yeh, H. Y..(2010).Experimental study of micro-cracks in stress corrosion of fiber reinforced composites.. |
| MLA | Dai, Jianjun,et al."Experimental study of micro-cracks in stress corrosion of fiber reinforced composites".(2010). |