Failure Behavior of Plasma-Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coatings Under Three-Point Bending Test via Acoustic Emission Technique | |
Wang, L.1; Ni, J. X.1; Shao, F.1; Yang, J. S.1,2; Zhong, X. H.1; Zhao, H. Y.1; Liu, C. G.1; Tao, S. Y.1; Wang, Y.3; Li, D. Y.4 | |
刊名 | JOURNAL OF THERMAL SPRAY TECHNOLOGY |
2017 | |
卷号 | 26期号:1-2页码:116-131 |
关键词 | acoustic emission (AE) failure plasma spraying thermal barrier coatings three-point bending (3PB) |
英文摘要 | In this paper, the failure behavior of plasma-sprayed yttria-stabilized zirconia thermal barrier coatings fabricated by atmospheric plasma spraying (APS-TBCs) under three-point bending (3PB) test has been characterized via acoustic emission (AE) technique. Linear positioning method has been adopted to monitor dynamic failure process of the APS-TBCs under 3PB test. The investigation results indicate that the variation of AE parameters (AE event counts, amplitudes and AE energy) corresponds well with the change of stress-strain curve of the loading processes. The failure mechanism was analyzed based on the characteristics of AE parameters. The distribution of frequency of crack propagation has been obtained. The AE signals came from two aspects: i.e., plastic deformation of substrates, initiation and propagation of the cracks in the coatings. The AE analysis combined with cross-sectional observation has indicated that many critical cracks initiate at the surface of the top-coat. And some main cracks tend to propagate toward the substrate/bond-coat interface. The actual failure mechanism of the APS-TBCs under 3PB test is attributed to the debonding of metallic coating from the substrates and the propagation of the horizontal crack along the substrate/bond-coat interface under the action of flexural moment. |
WOS标题词 | Science & Technology ; Technology |
类目[WOS] | Materials Science, Coatings & Films |
研究领域[WOS] | Materials Science |
关键词[WOS] | IMPEDANCE SPECTROSCOPY ; BOND COAT ; PS-PVD ; CYCLING BEHAVIOR ; DURABILITY ; SUSPENSION ; TGO |
收录类别 | SCI ; ISTP |
语种 | 英语 |
WOS记录号 | WOS:000392060300012 |
内容类型 | 期刊论文 |
源URL | [http://ir.sic.ac.cn/handle/331005/23374] |
专题 | 上海硅酸盐研究所_特种无机涂层重点实验室_期刊论文 |
作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, Key Lab Inorgan Coating Mat CAS, Shanghai 201899, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100039, Peoples R China 3.Harbin Inst Technol, Sch Mat Sci & Engn, Lab Nano Surface Engn, Harbin 150001, Peoples R China 4.Univ Alberta, Dept Chem & Mat Engn, Edmonton, AB T6G2V4, Canada |
推荐引用方式 GB/T 7714 | Wang, L.,Ni, J. X.,Shao, F.,et al. Failure Behavior of Plasma-Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coatings Under Three-Point Bending Test via Acoustic Emission Technique[J]. JOURNAL OF THERMAL SPRAY TECHNOLOGY,2017,26(1-2):116-131. |
APA | Wang, L..,Ni, J. X..,Shao, F..,Yang, J. S..,Zhong, X. H..,...&Li, D. Y..(2017).Failure Behavior of Plasma-Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coatings Under Three-Point Bending Test via Acoustic Emission Technique.JOURNAL OF THERMAL SPRAY TECHNOLOGY,26(1-2),116-131. |
MLA | Wang, L.,et al."Failure Behavior of Plasma-Sprayed Yttria-Stabilized Zirconia Thermal Barrier Coatings Under Three-Point Bending Test via Acoustic Emission Technique".JOURNAL OF THERMAL SPRAY TECHNOLOGY 26.1-2(2017):116-131. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论