Effect of heat treatment on the mechanical properties of TiAl alloy | |
Liu J(刘军); Hu YL(胡玉兰); Qiao HC(乔红超); Zhao JB(赵吉宾) | |
2016 | |
会议名称 | International Conference on Innovative Material Science and Technology (IMST) |
会议日期 | Augest 19-21, 2016 |
会议地点 | Shenzhen, China |
关键词 | TiAl alloy heat treatment grain refining micro hardness lanthanum |
页码 | 359-364 |
通讯作者 | 刘军 |
中文摘要 | Heat treatment can influence the microstructure and mechanical properties, in order to homogenize the composition and microstructure, improve the mechanical properties, Ti44Al6Nb0.9La alloy was heat treated at different temperatures and cooling conditions. The experimental results showed that macro-grains grew larger with the elevated temperature. The near-lamellar microstructure was obtained after heat treatment of 1200 degrees C for 2 hours, which transformed into fully-lamellar microstructure as the temperature rose. In addition, linear and lumpish lanthanum compounds were located at inter-lamellae and the colony boundaries, which accumulated more with the accelerated temperature. Micro-hardness test indicated the value of micro-hardness increased differently and the value was the relative maximum when the temperature was 1270 degrees C, as a result of solution strengthening of Nb and precipitation strengthening of La. |
收录类别 | CPCI(ISTP) |
产权排序 | 2 |
会议录 | PROCEEDINGS OF THE 2016 INTERNATIONAL CONFERENCE ON INNOVATIVE MATERIAL SCIENCE AND TECHNOLOGY (IMST 2016) |
会议录出版者 | ATLANTIS PRESS |
会议录出版地 | PARIS |
语种 | 英语 |
ISSN号 | 1951-6851 |
ISBN号 | 978-94-6252-269-5 |
WOS记录号 | WOS:000391726800053 |
内容类型 | 会议论文 |
源URL | [http://ir.sia.cn/handle/173321/19849] |
专题 | 沈阳自动化研究所_装备制造技术研究室 |
推荐引用方式 GB/T 7714 | Liu J,Hu YL,Qiao HC,et al. Effect of heat treatment on the mechanical properties of TiAl alloy[C]. 见:International Conference on Innovative Material Science and Technology (IMST). Shenzhen, China. Augest 19-21, 2016. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论