YVO_4晶体缺陷分析 | |
邹宇琦; 李新军; 徐军; 干福熹; 田玉莲; 黄万霞 | |
刊名 | 人工晶体学报
![]() |
2002 | |
卷号 | 31期号:1页码:14 |
其他题名 | Study on Defects of YVO_4 Crystal |
中文摘要 | 运用同步辐射白光X射线形貌术分析了YVO_4的结构和缺陷行为,也观测了YVO_4晶体(001)、(100)面的缺陷。发现在(001)面出现应力生长区、沿[001]方向的位错线以及晶体中镶嵌结构。运用白光形貌术拍摄到的劳埃斑,证明晶体为四方晶系。确定了小角晶界是引起多晶的主要原因。采用电子探针仪分析了散射颗粒形成是由杂质铁和铝的引入造成。 |
英文摘要 | X-ray topography was used to investigate the structure and defects of YVO_4 crystal. Dislocations were detected on both planes of (001) and (100) of YVO_4 crystal, as well as mosaic structure and stress area on some samples. The cause of formation of YVO_4 crystal was analyzed. Laue spots were clearly displayed by using X-ray topography, which were shown that YVO_4 crystal was conforming to tetragonal structure. Some defect spots on (001) by using EPMA demonstrated that relatively slight amount of ferrum and aluminum existed in these areas. |
收录类别 | EI |
语种 | 中文 |
内容类型 | 期刊论文 |
版本 | 出版稿 |
源URL | [http://ir.siom.ac.cn/handle/181231/17935] ![]() |
专题 | 上海光学精密机械研究所_激光与光电子功能材料研发中心 |
作者单位 | 1.邹宇琦, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 2.徐军, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 3.干福熹, 中国科学院上海光学精密机械研究所, 上海 201800, 中国. 4.李新军, 上海大学, 上海 201800, 中国. 5.田玉莲, 中国科学院北京高能物理研究所, 国家同步辐射实验室, 北京 100039, 中国. 6.黄万霞, 中国科学院北京高能物理研究所, 国家同步辐射实验室, 北京 100039, 中国. |
推荐引用方式 GB/T 7714 | 邹宇琦,李新军,徐军,等. YVO_4晶体缺陷分析[J]. 人工晶体学报,2002,31(1):14. |
APA | 邹宇琦,李新军,徐军,干福熹,田玉莲,&黄万霞.(2002).YVO_4晶体缺陷分析.人工晶体学报,31(1),14. |
MLA | 邹宇琦,et al."YVO_4晶体缺陷分析".人工晶体学报 31.1(2002):14. |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论