Effects of heating conditions on the microstructure and superconducting properties of Sr0.6K0.4Fe2As2 | |
Ma YW(马衍伟) | |
刊名 | SUPERCONDUCTOR SCIENCE & TECHNOLOGY |
2010 | |
通讯作者 | 马衍伟 |
中文摘要 | We report a study on the effect of sintering temperature on the microstructure and superconducting properties of Sr0.6K0.4Fe2As2 bulk samples, which were synthesized by the one-step solid reaction method. The heat treatment temperatures were varied from 700 to 900 degrees C in an argon atmosphere. It was found that the annealing temperature had little influence on the critical temperature T-c. However, the irreversibility field H-irr and critical current density J(c) were significantly affected by the sintering temperature; for instance, the J(c) at both 5 and 20 K increased with increasing the synthesis temperatures up to 850 degrees C, and then further increasing the temperature hardly affected the J(c) improvement. In addition, samples heat treated at temperatures over 850 degrees C exhibited a very weak J(c)-field dependence, especially at 20 K. Characterizations revealed that high temperature sintering resulted in large grains with fewer impurities. |
学科主题 | 材料合成与加工工艺 |
收录类别 | 1 |
公开日期 | 2010-09-29 |
附注 | We report a study on the effect of sintering temperature on the microstructure and superconducting properties of Sr0.6K0.4Fe2As2 bulk samples, which were synthesized by the one-step solid reaction method. The heat treatment temperatures were varied from 700 to 900 degrees C in an argon atmosphere. It was found that the annealing temperature had little influence on the critical temperature T-c. However, the irreversibility field H-irr and critical current density J(c) were significantly affected by the sintering temperature; for instance, the J(c) at both 5 and 20 K increased with increasing the synthesis temperatures up to 850 degrees C, and then further increasing the temperature hardly affected the J(c) improvement. In addition, samples heat treated at temperatures over 850 degrees C exhibited a very weak J(c)-field dependence, especially at 20 K. Characterizations revealed that high temperature sintering resulted in large grains with fewer impurities. |
内容类型 | 期刊论文 |
源URL | [http://ir.iee.ac.cn/handle/311042/399] |
专题 | 电工研究所_超导材料及强磁场科学研究组_超导材料及强磁场科学研究组_期刊论文 |
推荐引用方式 GB/T 7714 | Ma YW. Effects of heating conditions on the microstructure and superconducting properties of Sr0.6K0.4Fe2As2[J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY,2010. |
APA | 马衍伟.(2010).Effects of heating conditions on the microstructure and superconducting properties of Sr0.6K0.4Fe2As2.SUPERCONDUCTOR SCIENCE & TECHNOLOGY. |
MLA | 马衍伟."Effects of heating conditions on the microstructure and superconducting properties of Sr0.6K0.4Fe2As2".SUPERCONDUCTOR SCIENCE & TECHNOLOGY (2010). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论