Strongly enhanced critical current density in MgB2/Fe tapes by stearic acid and stearate doping | |
Ma YW(马衍伟) | |
刊名 | SUPERCONDUCTOR SCIENCE & TECHNOLOGY
![]() |
2007 | |
通讯作者 | 马衍伟 |
中文摘要 | Fe-sheathed MgB2 tapes with cheap stearic acid, Mg stearate and Zn stearate doping were prepared through the in situ powder-in-tube method. It is found that J(c), H-irr and H-c2 were significantly enhanced by doping. Compared to the pure tapes, J(c) for all the doped samples was improved by more than an order of magnitude in a high-field regime. At 4.2 K, the transport J(c) reached 2.02 x 10(4) A cm(-2) at 10 T for the Zn stearate doped tapes and 3.72 x 10(3) A cm(-2) at 14 T for the stearic acid doped samples, respectively. Moreover, at 20 K, H-irr for the Zn stearate doped tape achieved 10 T, which is comparable to that of the commercial NbTi at 4.2 K. The improvement of J(c)-H properties in doped samples can be attributed to the increase of H-c2 resulting from the incorporation of C atoms into the MgB2 crystal lattice as well as a high density of flux-pinning centres. |
学科主题 | 材料合成与加工工艺 |
收录类别 | 1 |
公开日期 | 2010-09-29 |
附注 | Fe-sheathed MgB2 tapes with cheap stearic acid, Mg stearate and Zn stearate doping were prepared through the in situ powder-in-tube method. It is found that J(c), H-irr and H-c2 were significantly enhanced by doping. Compared to the pure tapes, J(c) for all the doped samples was improved by more than an order of magnitude in a high-field regime. At 4.2 K, the transport J(c) reached 2.02 x 10(4) A cm(-2) at 10 T for the Zn stearate doped tapes and 3.72 x 10(3) A cm(-2) at 14 T for the stearic acid doped samples, respectively. Moreover, at 20 K, H-irr for the Zn stearate doped tape achieved 10 T, which is comparable to that of the commercial NbTi at 4.2 K. The improvement of J(c)-H properties in doped samples can be attributed to the increase of H-c2 resulting from the incorporation of C atoms into the MgB2 crystal lattice as well as a high density of flux-pinning centres. |
内容类型 | 期刊论文 |
源URL | [http://ir.iee.ac.cn/handle/311042/319] ![]() |
专题 | 电工研究所_超导材料及强磁场科学研究组_超导材料及强磁场科学研究组_期刊论文 |
推荐引用方式 GB/T 7714 | Ma YW. Strongly enhanced critical current density in MgB2/Fe tapes by stearic acid and stearate doping[J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY,2007. |
APA | 马衍伟.(2007).Strongly enhanced critical current density in MgB2/Fe tapes by stearic acid and stearate doping.SUPERCONDUCTOR SCIENCE & TECHNOLOGY. |
MLA | 马衍伟."Strongly enhanced critical current density in MgB2/Fe tapes by stearic acid and stearate doping".SUPERCONDUCTOR SCIENCE & TECHNOLOGY (2007). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论