Systematic study of the microstructures and electrical and superconducting properties of nanocarbon doped MgB2 tapes | |
Ma YW(马衍伟) | |
刊名 | SUPERCONDUCTOR SCIENCE & TECHNOLOGY |
2007 | |
通讯作者 | 马衍伟 |
中文摘要 | A series of C doped and undoped MgB2 tapes sintered at 600 -950 degrees C was fabricated. The relationships between the critical current properties, crystallinity and microstructures were systematically studied as functions of the C doping level and heating conditions. A decrease in the a-axis length due to carbon substitution was observed in the C doped samples. The full width at half maximum (FWHM) of the MgB2 (101) peak increased with increasing C doping level, suggesting that the introduction of lattice defects and/or the decrease of the grain size of MgB2 occurred on C doping. Due to the substitution of C for B, the upper critical field was improved in C doped MgB2 samples. Substantially improved critical current density, J(c), was found in all of the C doped samples. At 4.2 K, 10 T, J(c) reached 2.2 x 104 A cm(-2) in the 8% C doped samples. |
学科主题 | 材料合成与加工工艺 |
收录类别 | 1 |
公开日期 | 2010-09-29 |
附注 | A series of C doped and undoped MgB2 tapes sintered at 600 -950 degrees C was fabricated. The relationships between the critical current properties, crystallinity and microstructures were systematically studied as functions of the C doping level and heating conditions. A decrease in the a-axis length due to carbon substitution was observed in the C doped samples. The full width at half maximum (FWHM) of the MgB2 (101) peak increased with increasing C doping level, suggesting that the introduction of lattice defects and/or the decrease of the grain size of MgB2 occurred on C doping. Due to the substitution of C for B, the upper critical field was improved in C doped MgB2 samples. Substantially improved critical current density, J(c), was found in all of the C doped samples. At 4.2 K, 10 T, J(c) reached 2.2 x 104 A cm(-2) in the 8% C doped samples. |
内容类型 | 期刊论文 |
源URL | [http://ir.iee.ac.cn/handle/311042/303] |
专题 | 电工研究所_超导材料及强磁场科学研究组_超导材料及强磁场科学研究组_期刊论文 |
推荐引用方式 GB/T 7714 | Ma YW. Systematic study of the microstructures and electrical and superconducting properties of nanocarbon doped MgB2 tapes[J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY,2007. |
APA | 马衍伟.(2007).Systematic study of the microstructures and electrical and superconducting properties of nanocarbon doped MgB2 tapes.SUPERCONDUCTOR SCIENCE & TECHNOLOGY. |
MLA | 马衍伟."Systematic study of the microstructures and electrical and superconducting properties of nanocarbon doped MgB2 tapes".SUPERCONDUCTOR SCIENCE & TECHNOLOGY (2007). |
个性服务 |
查看访问统计 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论